EN 10025-2 S235J0 vs CSA G40.21 400A

Related Material — 58.2% match based on chemical composition and mechanical property overlap.

EN 10025-2 S235J0 (EN 10025-2:2019) and CSA G40.21 400A (CSA G40.21-13 (R2023)) are both steel grades. Both fall under the Structural Steel category. EN 10025-2 S235J0 is typically used for used for structural beams, bridges, frames, plates, construction equipment, and welded structures., while CSA G40.21 400A is commonly used for atmospheric corrosion-resistant (weathering) structural steel; exposed bridge girders and structural members where high strength and weathering resistance are both needed. EN 10025-2 S235J0 is defined under European Standard (EN), originating from Europe, while CSA G40.21 400A is defined under Canadian Standards Association (CSA), originating from Canada.

As per chemical composition, EN 10025-2 S235J0 vs CSA G40.21 400A is a 87.2% match. As per mechanical properties, the match is 0%. Combined, this makes them a related material overall at 58.2%.

Frequently Compared With EN 10025-2 S235J0:
CSA G40.21 260W CSA G40.21 400W CSA G40.21 480W CSA G40.21 350W CSA G40.21 300W AS/NZS 3679.1 300 AS/NZS 3679.1 350 GOST 19281 09G2S ASTM A1008 SS Grade 80 ASTM A283C ASTM A1008 SS Grade 50 ASTM A572 Gr.65
Match Breakdown
CHEMISTRY MATCH
87.2%
MECHANICAL MATCH
0%
OVERALL
58.2%
Specifications
Property EN 10025-2 S235J0 CSA G40.21 400A
Standard EN 10025-2:2019 CSA G40.21-13 (R2023)
Category Structural Steel Structural Steel
C (%) <=0.17 <=0.23
Mn (%) <=1.40 <=1.60
P (%) <=0.030 <=0.035
S (%) <=0.030 <=0.035
N (%) <=0.012 Not specified
Cu (%) <=0.55 0.20-0.40
Si (%) Not specified <=0.40
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property EN 10025-2 S235J0 CSA G40.21 400A
Tensile Strength 360-510 MPa 520-670 MPa
Yield Strength >=235 MPa 400 MPa min
Elongation >=26% 17% min
Condition Nominal thickness up to 16 mm (tensile for 3 to 100 mm, elongation for 3 to 40 mm), longitudinal test pieces Not specified
Impact Not specified 27J at 0°C
Typical Applications
EN 10025-2 S235J0
Used for structural beams, bridges, frames, plates, construction equipment, and welded structures.
CSA G40.21 400A
Atmospheric corrosion-resistant (weathering) structural steel; exposed bridge girders and structural members where high strength and weathering resistance are both needed
Key Differences
Can EN 10025-2 S235J0 Be Substituted With CSA G40.21 400A?
EN 10025-2 S235J0 and CSA G40.21 400A share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
EN 10025-2 S235J0
Plate → (2 listings)
Thickness: 10–10 mm (0.39–0.39 in)
Width: 1500–1500 mm (59.06–59.06 in)
Length: 3900–4400 mm (153.54–173.23 in)
CSA G40.21 400A
Plate → (2 listings)
Thickness: 10–10 mm (0.39–0.39 in)
Width: 1500–1500 mm (59.06–59.06 in)
Length: 2800–4200 mm (110.24–165.35 in)
On M-EX Right Now
EN 10025-2 S235J0
2 active listings and RFQs →
CSA G40.21 400A
2 active listings and RFQs →
Frequently Asked Questions
What is the difference between EN 10025-2 S235J0 and CSA G40.21 400A?
EN 10025-2 S235J0 specifies N which is not specified for CSA G40.21 400A. CSA G40.21 400A specifies Si which is not specified for EN 10025-2 S235J0.
Can EN 10025-2 S235J0 be substituted with CSA G40.21 400A?
EN 10025-2 S235J0 and CSA G40.21 400A share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.