EN 10025-2 S235J0 vs CSA G40.21 400W

Related Material — 57.5% match based on chemical composition and mechanical property overlap.

EN 10025-2 S235J0 (EN 10025-2:2019) and CSA G40.21 400W (CSA G40.21-13 (R2023)) are both steel grades. Both fall under the Structural Steel category. EN 10025-2 S235J0 is typically used for used for structural beams, bridges, frames, plates, construction equipment, and welded structures., while CSA G40.21 400W is commonly used for heavy structural fabrication, bridges, offshore platforms, cranes, pressure vessels, mining equipment.. EN 10025-2 S235J0 is defined under European Standard (EN), originating from Europe, while CSA G40.21 400W is defined under Canadian Standards Association (CSA), originating from Canada.

As per chemical composition, EN 10025-2 S235J0 vs CSA G40.21 400W is a 86.3% match. As per mechanical properties, the match is 0%. Combined, this makes them a related material overall at 57.5%.

Frequently Compared With EN 10025-2 S235J0:
CSA G40.21 260W CSA G40.21 480W CSA G40.21 300W CSA G40.21 350W CSA G40.21 400A AS/NZS 3679.1 300 AS/NZS 3679.1 350 GOST 19281 09G2S ASTM A283C ASTM A1008 SS Grade 50 ASTM A1008 SS Grade 80 ASTM A572 Gr.65
Match Breakdown
CHEMISTRY MATCH
86.3%
MECHANICAL MATCH
0%
OVERALL
57.5%
Specifications
Property EN 10025-2 S235J0 CSA G40.21 400W
Standard EN 10025-2:2019 CSA G40.21-13 (R2023)
Category Structural Steel Structural Steel
C (%) <=0.17 max 0.23
Mn (%) <=1.40 max 1.6
P (%) <=0.030 max 0.035
S (%) <=0.030 max 0.035
N (%) <=0.012 Not specified
Cu (%) <=0.55 Not specified
Si (%) Not specified max 0.5
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property EN 10025-2 S235J0 CSA G40.21 400W
Tensile Strength 360-510 MPa 520-690 MPa
Yield Strength >=235 MPa 400 MPa min
Elongation >=26% Not specified
Condition Nominal thickness up to 16 mm (tensile for 3 to 100 mm, elongation for 3 to 40 mm), longitudinal test pieces Not specified
Typical Applications
EN 10025-2 S235J0
Used for structural beams, bridges, frames, plates, construction equipment, and welded structures.
CSA G40.21 400W
Heavy structural fabrication, bridges, offshore platforms, cranes, pressure vessels, mining equipment.
Key Differences
Can EN 10025-2 S235J0 Be Substituted With CSA G40.21 400W?
EN 10025-2 S235J0 and CSA G40.21 400W share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
EN 10025-2 S235J0
Plate → (2 listings)
Thickness: 10–10 mm (0.39–0.39 in)
Width: 1500–1500 mm (59.06–59.06 in)
Length: 3900–4400 mm (153.54–173.23 in)
CSA G40.21 400W
Plate → (2 listings)
Thickness: 10–10 mm (0.39–0.39 in)
Width: 1500–1500 mm (59.06–59.06 in)
Length: 2500–5200 mm (98.43–204.72 in)
On M-EX Right Now
EN 10025-2 S235J0
2 active listings and RFQs →
CSA G40.21 400W
2 active listings and RFQs →
Frequently Asked Questions
What is the difference between EN 10025-2 S235J0 and CSA G40.21 400W?
EN 10025-2 S235J0 specifies N, Cu which are not specified for CSA G40.21 400W. CSA G40.21 400W specifies Si which is not specified for EN 10025-2 S235J0.
Can EN 10025-2 S235J0 be substituted with CSA G40.21 400W?
EN 10025-2 S235J0 and CSA G40.21 400W share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.