Strong Match — 92% match based on chemical composition and mechanical property overlap.

EN 10025-2 S275JR (EN 10025-2:2019) and EN 10025-2 S275 (EN 10025-2:2019) are both steel grades. Both fall under the Structural Steel category. EN 10025-2 S275JR is typically used for general structural work, bridges, machinery frames, while EN 10025-2 S275 is commonly used for structural beams, columns, bridges, general fabrication. EN 10025-2 S275JR is defined under European Standard (EN), originating from Europe, while EN 10025-2 S275 is defined under European Standard (EN), originating from Europe.

As per chemical composition, EN 10025-2 S275JR vs EN 10025-2 S275 is a 88% match. As per mechanical properties, the match is 100%. Combined, this makes them a strong match overall at 92%.

Frequently Compared With EN 10025-2 S275JR:
CSA G40.21 400W CSA G40.21 480W ASTM A283C GOST 19281 09G2S CSA G40.21 260W AS/NZS 3679.1 300 CSA G40.21 300W AS/NZS 3679.1 350 CSA G40.21 350W CSA G40.21 400A ASTM A1008 SS Grade 50 ASTM A1008 SS Grade 80
Match Breakdown
CHEMISTRY MATCH
88%
MECHANICAL MATCH
100%
OVERALL
92%
Specifications
Property EN 10025-2 S275JR EN 10025-2 S275
Standard EN 10025-2:2019 EN 10025-2:2019
Category Structural Steel Structural Steel
C (%) <=0.21 0-0.25
Mn (%) <=1.50 0-1.5
P (%) <=0.035 max 0.04
S (%) <=0.035 max 0.04
N (%) <=0.012 Not specified
Cu (%) <=0.55 Not specified
Si (%) Not specified 0-0.5
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property EN 10025-2 S275JR EN 10025-2 S275
Tensile Strength 410-560 MPa 410-560 MPa
Yield Strength >=275 MPa 275 MPa min (t<=16mm)
Elongation >=23% 23% min
Condition Nominal thickness up to 16 mm (tensile for 3 to 100 mm, elongation for 3 to 40 mm), longitudinal test pieces Not specified
Typical Applications
EN 10025-2 S275JR
General structural work, bridges, machinery frames
EN 10025-2 S275
Structural beams, columns, bridges, general fabrication
Key Differences
Can EN 10025-2 S275JR Be Substituted With EN 10025-2 S275?
EN 10025-2 S275JR and EN 10025-2 S275 overlap closely enough on chemistry and mechanical properties that EN 10025-2 S275 is often considered as a substitute for EN 10025-2 S275JR in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
Forms & Sizes Available on M-EX
EN 10025-2 S275JR
Plate → (3 listings)
Thickness: 10–10 mm (0.39–0.39 in)
Width: 1500–1500 mm (59.06–59.06 in)
Length: 3000–3500 mm (118.11–137.8 in)
EN 10025-2 S275
Round Bar → (2 listings)
Diameter: 40–40 mm (1.57–1.57 in)
Length: 5000–5000 mm (196.85–196.85 in)
On M-EX Right Now
EN 10025-2 S275JR
3 active listings and RFQs →
EN 10025-2 S275
2 active listings and RFQs →
Frequently Asked Questions
What is the difference between EN 10025-2 S275JR and EN 10025-2 S275?
EN 10025-2 S275JR specifies N, Cu which are not specified for EN 10025-2 S275. EN 10025-2 S275 specifies Si which is not specified for EN 10025-2 S275JR.
Can EN 10025-2 S275JR be substituted with EN 10025-2 S275?
EN 10025-2 S275JR and EN 10025-2 S275 overlap closely enough on chemistry and mechanical properties that EN 10025-2 S275 is often considered as a substitute for EN 10025-2 S275JR in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.