Close Alternative — 80.2% match
based on chemical composition and mechanical property overlap.
EN 10025-2 S275JR (EN 10025-2:2019) and GB/T 700 Q275C (GB/T 700:2006) are both steel grades.
Both fall under the Structural Steel category.
EN 10025-2 S275JR is typically used for general structural work, bridges, machinery frames, while GB/T 700 Q275C is commonly used for hot rolled structural sheets, strips, sections and bars for welding, riveting and bolting engineering.
EN 10025-2 S275JR is defined under European Standard (EN), originating from Europe, while GB/T 700 Q275C is defined under Guobiao Standards (GB/T), originating from China.
As per chemical composition, EN 10025-2 S275JR vs GB/T 700 Q275C is a 89.2% match.
As per mechanical properties, the match is 62.2%.
Combined, this makes them a close alternative overall at 80.2%.
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
EN 10025-2 S275JR
GB/T 700 Q275C
Tensile Strength
410-560 MPa
410-540 MPa
Yield Strength
>=275 MPa
>=275 MPa
Elongation
>=23%
>=22%
Condition
Nominal thickness up to 16 mm (tensile for 3 to 100 mm, elongation for 3 to 40 mm), longitudinal test pieces
Hot rolled, controlled rolled or normalized; yield up to 16 mm, elongation up to 40 mm (N/mm2 = MPa)
Typical Applications
EN 10025-2 S275JR
General structural work, bridges, machinery frames
GB/T 700 Q275C
Hot rolled structural sheets, strips, sections and bars for welding, riveting and bolting engineering
Key Differences
EN 10025-2 S275JR specifies N, Cu which are not specified for GB/T 700 Q275C.
GB/T 700 Q275C specifies Si which is not specified for EN 10025-2 S275JR.
Can EN 10025-2 S275JR Be Substituted With GB/T 700 Q275C?
EN 10025-2 S275JR and GB/T 700 Q275C are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
What is the difference between EN 10025-2 S275JR and GB/T 700 Q275C?
EN 10025-2 S275JR specifies N, Cu which are not specified for GB/T 700 Q275C. GB/T 700 Q275C specifies Si which is not specified for EN 10025-2 S275JR.
Can EN 10025-2 S275JR be substituted with GB/T 700 Q275C?
EN 10025-2 S275JR and GB/T 700 Q275C are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.