Minimal Match — 35% match
based on chemical composition and mechanical property overlap.
EN 10025-3 S355N (EN 10025-3:2019) and ASTM A1008 SS Grade 80 (ASTM A1008) are both steel grades.
Both fall under the Structural Steel category.
EN 10025-3 S355N is defined under European Standard (EN), originating from Europe, while ASTM A1008 SS Grade 80 is defined under ASTM International, originating from United States.
As per chemical composition, EN 10025-3 S355N vs ASTM A1008 SS Grade 80 is a 63.5% match.
As per mechanical properties, the match is 0%.
Combined, this makes them a minimal match overall at 35%.
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
EN 10025-3 S355N
ASTM A1008 SS Grade 80
Tensile Strength
470-630 MPa
570 MPa min
Yield Strength
>=355 MPa
550 MPa min
Elongation
>=22%
10% min
Condition
Normalized or normalized rolled (N), nominal thickness up to 16 mm (tensile strength up to 100 mm), Table 4
EN 10025-3 S355N specifies Nb, V, Ni, N which are not specified for ASTM A1008 SS Grade 80.
Can EN 10025-3 S355N Be Substituted With ASTM A1008 SS Grade 80?
EN 10025-3 S355N and ASTM A1008 SS Grade 80 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
What is the difference between EN 10025-3 S355N and ASTM A1008 SS Grade 80?
EN 10025-3 S355N specifies Nb, V, Ni, N which are not specified for ASTM A1008 SS Grade 80.
Can EN 10025-3 S355N be substituted with ASTM A1008 SS Grade 80?
EN 10025-3 S355N and ASTM A1008 SS Grade 80 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.