EN 10025-5 S235J2W vs ASTM A588

Minimal Match — 35% match based on chemical composition and mechanical property overlap.

EN 10025-5 S235J2W (EN 10025-5:2019) and ASTM A588 (ASTM A588) are both steel grades. Both fall under the Structural Steel (Corten / Weathering) category. EN 10025-5 S235J2W is typically used for weathering (atmospheric corrosion-resistant) structural steel; bridges, railway wagons, shipping containers, transmission towers, outdoor structures exposed without protective coating, while ASTM A588 is commonly used for used for bridges, railway wagons, transmission poles, architectural structures, containers, and outdoor construction.. EN 10025-5 S235J2W is defined under European Standard (EN), originating from Europe, while ASTM A588 is defined under ASTM International, originating from United States.

As per chemical composition, EN 10025-5 S235J2W vs ASTM A588 is a 72.7% match. As per mechanical properties, the match is 3.1%. Combined, this makes them a minimal match overall at 35%.

Frequently Compared With EN 10025-5 S235J2W:
EN 10025-5 S355J2WP CSA G40.21 350A EN 10025-5 S355J2W ASTM A588 Grade A EN 10025-5 S355J0WP CSA G40.21 260WT CSA G40.21 50W JIS G3114 SMA400 AS/NZS 3678 Grade 350WR ASTM A709 Grade HPS 70W ASTM A588 Grade B CSA G40.21 480A
Match Breakdown
CHEMISTRY MATCH
72.7%
MECHANICAL MATCH
3.1%
OVERALL
35%
Specifications
Property EN 10025-5 S235J2W ASTM A588
Standard EN 10025-5:2019 ASTM A588
Category Structural Steel (Corten / Weathering) Structural Steel (Corten / Weathering)
C (%) <=0.13 0.19 max
Si (%) <=0.40 0.30-0.65
Mn (%) 0.20-0.60 0.80-1.25
P (%) <=0.035 0.04 max
S (%) <=0.030 0.05 max
Cr (%) 0.40-0.80 0.40-0.70
Cu (%) 0.25-0.55 0.20-0.40
Ni (%) Not specified 0.40 max
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property EN 10025-5 S235J2W ASTM A588
Tensile Strength 360-510 MPa 485-630 MPa
Yield Strength >=235 MPa 345 MPa min
Elongation >=26% 18-21%
Condition Nominal thickness up to 16 mm for yield, 3 to 100 mm for tensile, 3 to 40 mm for elongation (Lo = 5.65 sqrt(S0), longitudinal); transverse values are lower, see blocks Not specified
Hardness Not specified 140-190 HB
Typical Applications
EN 10025-5 S235J2W
Weathering (atmospheric corrosion-resistant) structural steel; bridges, railway wagons, shipping containers, transmission towers, outdoor structures exposed without protective coating
ASTM A588
Used for bridges, railway wagons, transmission poles, architectural structures, containers, and outdoor construction.
Key Differences
Can EN 10025-5 S235J2W Be Substituted With ASTM A588?
EN 10025-5 S235J2W and ASTM A588 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
EN 10025-5 S235J2W
Plate → (2 listings)
Thickness: 10–10 mm (0.39–0.39 in)
Width: 1500–1500 mm (59.06–59.06 in)
Length: 2800–3600 mm (110.24–141.73 in)
ASTM A588
Plate → (2 listings)
Thickness: 10–10 mm (0.39–0.39 in)
Width: 1500–1500 mm (59.06–59.06 in)
Length: 2500–2700 mm (98.43–106.3 in)
On M-EX Right Now
EN 10025-5 S235J2W
2 active listings and RFQs →
ASTM A588
2 active listings and RFQs →
Frequently Asked Questions
What is the difference between EN 10025-5 S235J2W and ASTM A588?
ASTM A588 specifies Ni which is not specified for EN 10025-5 S235J2W.
Can EN 10025-5 S235J2W be substituted with ASTM A588?
EN 10025-5 S235J2W and ASTM A588 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.