EN 10028-2 15NiCuMoNb5-6-4 vs GB/T 1591 Q460C

Related Material — 60.7% match based on chemical composition and mechanical property overlap.

EN 10028-2 15NiCuMoNb5-6-4 (EN 10028-2:2017) and GB/T 1591 Q460C (GB/T 1591:2018) are both steel grades. EN 10028-2 15NiCuMoNb5-6-4 is classified under Alloy Steel, while GB/T 1591 Q460C is classified under Structural Steel — a different category, which is worth noting alongside the chemistry match below. EN 10028-2 15NiCuMoNb5-6-4 is typically used for flat products for pressure purposes, while GB/T 1591 Q460C is commonly used for general structure for engineering (plates, strips, bars and sections). EN 10028-2 15NiCuMoNb5-6-4 is defined under European Standard (EN), originating from Europe, while GB/T 1591 Q460C is defined under Guobiao Standards (GB/T), originating from China.

As per chemical composition, EN 10028-2 15NiCuMoNb5-6-4 vs GB/T 1591 Q460C is a 54.1% match. As per mechanical properties, the match is 73.9%. Combined, this makes them a related material overall at 60.7%.

Frequently Compared With EN 10028-2 15NiCuMoNb5-6-4:
IS 1570 (Part 4) 103Cr4 IS 4367 07Cr4Mo6 IS 1570 (Part 4) 07Cr4Mo6 NF A35-565 100C6 UNI 11234 100Cr6 IS 1570 (Part 4) 103Cr6 IS 1570 (Part 4) 105Cr5 IS 1570 (Part 4) 10Cr20Mo6 IS 1570 (Part 7) 10Cr36Mo10H IS 4367 10Cr9Mo10 EN 10028-2 10CrMo9-10 IS 1570 (Part 4) 10Mo6
Match Breakdown
CHEMISTRY MATCH
54.1%
MECHANICAL MATCH
73.9%
OVERALL
60.7%
Specifications
Property EN 10028-2 15NiCuMoNb5-6-4 GB/T 1591 Q460C
Standard EN 10028-2:2017 GB/T 1591:2018
Category Alloy Steel Structural Steel
C (%) <=0.17 <=0.20
Si (%) 0.25-0.50 <=0.55
Mn (%) 0.80-1.20 <=1.80
P (%) <=0.025 <=0.030
S (%) <=0.010 <=0.030
Al (%) >=0.015 Not specified
N (%) <=0.020 <=0.015
Cr (%) <=0.30 <=0.30
Cu (%) 0.50-0.80 <=0.40
Mo (%) 0.25-0.50 <=0.20
Nb (%) 0.015-0.045 <=0.05
Ni (%) 1.00-1.30 <=0.80
V (%) Not specified <=0.13
Ti (%) Not specified <=0.05
B (%) Not specified <=0.004
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property EN 10028-2 15NiCuMoNb5-6-4 GB/T 1591 Q460C
Tensile Strength 610-780 MPa 550-720 MPa
Yield Strength >=460 MPa >=460 MPa
Elongation >=16% Not specified
Condition Usual delivery condition normalized and tempered (+NT), nominal thickness up to 40 mm; transverse direction, Yield Strength is ReH, Elongation is A Hot-rolled (as-rolled), nominal thickness or diameter up to 16 mm for yield; tensile strength for up to 100 mm
Typical Applications
EN 10028-2 15NiCuMoNb5-6-4
Flat products for pressure purposes
GB/T 1591 Q460C
General structure for engineering (plates, strips, bars and sections)
Key Differences
Can EN 10028-2 15NiCuMoNb5-6-4 Be Substituted With GB/T 1591 Q460C?
EN 10028-2 15NiCuMoNb5-6-4 and GB/T 1591 Q460C share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
EN 10028-2 15NiCuMoNb5-6-4
0 active listings and RFQs →
GB/T 1591 Q460C
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between EN 10028-2 15NiCuMoNb5-6-4 and GB/T 1591 Q460C?
Different category: EN 10028-2 15NiCuMoNb5-6-4 is Alloy Steel, GB/T 1591 Q460C is Structural Steel. EN 10028-2 15NiCuMoNb5-6-4 specifies Al which is not specified for GB/T 1591 Q460C. GB/T 1591 Q460C specifies V, Ti, B which are not specified for EN 10028-2 15NiCuMoNb5-6-4.
Can EN 10028-2 15NiCuMoNb5-6-4 be substituted with GB/T 1591 Q460C?
EN 10028-2 15NiCuMoNb5-6-4 and GB/T 1591 Q460C share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.