EN 10028-2 P235GH vs IS 1570 (Part 7) Fe360H

Related Material — 62.2% match based on chemical composition and mechanical property overlap.

EN 10028-2 P235GH (EN 10028-2:2017) and IS 1570 (Part 7) Fe360H (IS 1570 (Part 7):1992) are both steel grades. Both fall under the Carbon Steel category. EN 10028-2 P235GH is typically used for flat products for pressure purposes, while IS 1570 (Part 7) Fe360H is commonly used for boilers, pressure vessels, steam turbines, steam and water piping and other power plant equipment working at elevated temperature. EN 10028-2 P235GH is defined under European Standard (EN), originating from Europe, while IS 1570 (Part 7) Fe360H is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, EN 10028-2 P235GH vs IS 1570 (Part 7) Fe360H is a 76.7% match. As per mechanical properties, the match is 33.3%. Combined, this makes them a related material overall at 62.2%.

Frequently Compared With EN 10028-2 P235GH:
BS 970 (Part 1) 060A32 BS 970 (Part 1) 045A10 BS 970 (Part 1) 045M10 BS 970 (Part 1) 045A10 BS 970 (Part 3) 045A10 BS 970 (Part 1) 040A04 BS 970 (Part 1) 040A12 BS 970 (Part 1) 045M10 BS 970 (Part 3) 045M10 BS 970 (Part 1) 040A10 BS 970 (Part 1) 055M15 BS 970 (Part 1) 060A40
Match Breakdown
CHEMISTRY MATCH
76.7%
MECHANICAL MATCH
33.3%
OVERALL
62.2%
Specifications
Property EN 10028-2 P235GH IS 1570 (Part 7) Fe360H
Standard EN 10028-2:2017 IS 1570 (Part 7):1992
Category Carbon Steel Carbon Steel
C (%) <=0.16 <=0.20
Si (%) <=0.35 0.10-0.35
Mn (%) 0.60-1.20 0.40-1.20
P (%) <=0.025 <=0.03
S (%) <=0.010 <=0.03
Nb (%) <=0.030 Not specified
Al (%) >=0.020 Not specified
N (%) <=0.012 Not specified
Cr (%) <=0.30 <=0.25
Cu (%) <=0.30 <=0.30
Mo (%) <=0.08 <=0.10
Ni (%) <=0.30 <=0.30
Ti (%) <=0.03 Not specified
V (%) <=0.02 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property EN 10028-2 P235GH IS 1570 (Part 7) Fe360H
Tensile Strength 360-480 MPa 360-480 MPa
Yield Strength >=235 MPa >=205 MPa (0.2 % proof stress)
Elongation >=24% >=26%
Condition Usual delivery condition normalized (+N), nominal thickness up to 16 mm; transverse direction, Yield Strength is ReH, Elongation is A Plate, N, thickness over 3 to 16 (first row of Table 3)
Typical Applications
EN 10028-2 P235GH
Flat products for pressure purposes
IS 1570 (Part 7) Fe360H
Boilers, pressure vessels, steam turbines, steam and water piping and other power plant equipment working at elevated temperature
Key Differences
Can EN 10028-2 P235GH Be Substituted With IS 1570 (Part 7) Fe360H?
EN 10028-2 P235GH and IS 1570 (Part 7) Fe360H share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
EN 10028-2 P235GH
0 active listings and RFQs →
IS 1570 (Part 7) Fe360H
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between EN 10028-2 P235GH and IS 1570 (Part 7) Fe360H?
EN 10028-2 P235GH specifies Nb, Al, N, Ti which are not specified for IS 1570 (Part 7) Fe360H.
Can EN 10028-2 P235GH be substituted with IS 1570 (Part 7) Fe360H?
EN 10028-2 P235GH and IS 1570 (Part 7) Fe360H share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.