EN 10083-1 50CrMo4 vs IS 4367 07Cr4Mo6

Minimal Match — 35% match based on chemical composition and mechanical property overlap.

EN 10083-1 50CrMo4 (EN 10083-1:1991) and IS 4367 07Cr4Mo6 (IS 4367:1991) are both steel grades. Both fall under the Alloy Steel category. EN 10083-1 50CrMo4 is defined under European Standard (EN), originating from Europe, while IS 4367 07Cr4Mo6 is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, EN 10083-1 50CrMo4 vs IS 4367 07Cr4Mo6 is a 64.4% match. As per mechanical properties, the match is 0%. Combined, this makes them a minimal match overall at 35%.

Frequently Compared With EN 10083-1 50CrMo4:
IS 1570 (Part 4) 103Cr6 NF A35-565 100C6 IS 1570 (Part 4) 103Cr4 IS 1570 (Part 4) 07Cr4Mo6 IS 1570 (Part 4) 10Mo6 IS 11169 (Part 1) 10Ni5Cr4 IS 1570 (Part 4) 105Cr5 IS 1570 (Part 4) 10Cr20Mo6 IS 1570 (Part 7) 10Cr36Mo10H IS 1570 (Part 7) 10Mo6H UNI 11234 100Cr6 IS 4367 10Cr9Mo10
Match Breakdown
CHEMISTRY MATCH
64.4%
MECHANICAL MATCH
0%
OVERALL
35%
Specifications
Property EN 10083-1 50CrMo4 IS 4367 07Cr4Mo6
Standard EN 10083-1:1991 IS 4367:1991
Category Alloy Steel Alloy Steel
C (%) 0.46-0.54 <=0.12
Cr (%) 0.90-1.20 0.70-1.10
Mn (%) 0.50-0.80 0.40-0.70
Mo (%) 0.15-0.30 0.45-0.65
P (%) <=0.035 <=0.035
S (%) <=0.035 <=0.035
Si (%) <=0.40 0.15-0.60
Ni (%) Not specified <=0.30
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property EN 10083-1 50CrMo4 IS 4367 07Cr4Mo6
Condition Quenched and tempered, ruling section d <= 16 mm Normalised and tempered, ruling section up to 40 mm
Elongation 9% min >=19%
Hardness Soft annealed: 248 HB max Not specified
Tensile Strength 1100 to 1300 MPa 380-550 MPa
Yield Strength 900 MPa min 225 MPa min
Izod Impact Not specified 60 J min
Hardness (soft annealed) Not specified <=170 HB
Typical Applications
EN 10083-1 50CrMo4
Quenched and tempered machine parts; non alloy steels also normalized (clause 1)
IS 4367 07Cr4Mo6
Not documented
Key Differences
Can EN 10083-1 50CrMo4 Be Substituted With IS 4367 07Cr4Mo6?
EN 10083-1 50CrMo4 and IS 4367 07Cr4Mo6 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
EN 10083-1 50CrMo4
0 active listings and RFQs →
IS 4367 07Cr4Mo6
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between EN 10083-1 50CrMo4 and IS 4367 07Cr4Mo6?
IS 4367 07Cr4Mo6 specifies Ni which is not specified for EN 10083-1 50CrMo4.
Can EN 10083-1 50CrMo4 be substituted with IS 4367 07Cr4Mo6?
EN 10083-1 50CrMo4 and IS 4367 07Cr4Mo6 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.