Minimal Match — 35% match
based on chemical composition and mechanical property overlap.
EN 10083-1 36CrNiMo4 (EN 10083-1:1991) and GOST 4543 12HN3A (GOST 4543-2016) are both steel grades.
Both fall under the Alloy Steel category.
EN 10083-1 36CrNiMo4 is typically used for shafts, gears, high strength fasteners, while GOST 4543 12HN3A is commonly used for used for gears, pinions, crankshafts, aircraft parts, and transmission components..
EN 10083-1 36CrNiMo4 is defined under European Standard (EN) (Europe).
As per chemical composition, EN 10083-1 36CrNiMo4 vs GOST 4543 12HN3A is a 56.6% match.
As per mechanical properties, the match is 0%.
Combined, this makes them a minimal match overall at 35%.
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
EN 10083-1 36CrNiMo4
GOST 4543 12HN3A
Condition
Quenched and tempered, ruling section d <= 16 mm
Not specified
Elongation
10% min
11% min
Hardness
Soft annealed: 248 HB max
58-62 HRC (case)
Tensile Strength
1100 to 1300 MPa
850-1050 MPa
Yield Strength
900 MPa min
685 MPa min
Typical Applications
EN 10083-1 36CrNiMo4
Shafts, gears, high strength fasteners
GOST 4543 12HN3A
Used for gears, pinions, crankshafts, aircraft parts, and transmission components.
Key Differences
EN 10083-1 36CrNiMo4 specifies Mo, P, S which are not specified for GOST 4543 12HN3A.
Can EN 10083-1 36CrNiMo4 Be Substituted With GOST 4543 12HN3A?
EN 10083-1 36CrNiMo4 and GOST 4543 12HN3A share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
What is the difference between EN 10083-1 36CrNiMo4 and GOST 4543 12HN3A?
EN 10083-1 36CrNiMo4 specifies Mo, P, S which are not specified for GOST 4543 12HN3A.
Can EN 10083-1 36CrNiMo4 be substituted with GOST 4543 12HN3A?
EN 10083-1 36CrNiMo4 and GOST 4543 12HN3A share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.