Minimal Match — 35% match
based on chemical composition and mechanical property overlap.
EN 10084 15NiCr13 (EN 10084:2008) and UNI 11234 100Cr6 (UNI 11234:2007) are both steel grades.
Both fall under the Alloy Steel category.
EN 10084 15NiCr13 is typically used for heavily loaded gears, cams, camshafts, while UNI 11234 100Cr6 is commonly used for ball bearings,roller bearings,needle bearings,dies,punches,gauges,wear resistant components.
EN 10084 15NiCr13 is defined under European Standard (EN), originating from Europe, while UNI 11234 100Cr6 is defined under Ente Nazionale Italiano di Unificazione (UNI), originating from Italy.
As per chemical composition, EN 10084 15NiCr13 vs UNI 11234 100Cr6 is a 65.5% match.
As per mechanical properties, the match is 0%.
Combined, this makes them a minimal match overall at 35%.
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
EN 10084 15NiCr13
UNI 11234 100Cr6
Condition
Soft annealed
Not specified
Hardenability
+H band at 1.5 mm from the quenched end: 41 to 48 HRC
EN 10084 15NiCr13 specifies Ni which is not specified for UNI 11234 100Cr6.
Can EN 10084 15NiCr13 Be Substituted With UNI 11234 100Cr6?
EN 10084 15NiCr13 and UNI 11234 100Cr6 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
What is the difference between EN 10084 15NiCr13 and UNI 11234 100Cr6?
EN 10084 15NiCr13 specifies Ni which is not specified for UNI 11234 100Cr6.