EN 10084 20NiCrMo13-4 vs SAE J404 4320

Related Material — 67.3% match based on chemical composition and mechanical property overlap.

EN 10084 20NiCrMo13-4 (EN 10084:2008) and SAE J404 4320 (SAE J404:2009) are both steel grades. Both fall under the Alloy Steel category. EN 10084 20NiCrMo13-4 is typically used for case hardened machine parts: carburized or carbonitrided, then hardened (clause 3.1), while SAE J404 4320 is commonly used for used for gears, shafts, aircraft components, pinions, axles, and transmission parts.. EN 10084 20NiCrMo13-4 is defined under European Standard (EN), originating from Europe, while SAE J404 4320 is defined under SAE International, originating from United States.

As per chemical composition, EN 10084 20NiCrMo13-4 vs SAE J404 4320 is a 67.3% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a related material overall at 67.3%.

Frequently Compared With EN 10084 20NiCrMo13-4:
NF A35-565 100C6 UNI 11234 100Cr6 IS 1570 (Part 4) 103Cr4 IS 1570 (Part 4) 105Cr5 IS 4367 10Cr9Mo10 IS 1570 (Part 4) 10Mo6 IS 1570 (Part 4) 103Cr6 IS 1570 (Part 4) 10Cr20Mo6 IS 1570 (Part 4) 07Cr4Mo6 IS 1570 (Part 7) 10Mo6H IS 11169 (Part 1) 10Ni5Cr4 IS 4367 07Cr4Mo6
Match Breakdown
CHEMISTRY MATCH
67.3%
MECHANICAL MATCH
No shared data
OVERALL
67.3%
Specifications
Property EN 10084 20NiCrMo13-4 SAE J404 4320
Standard EN 10084:2008 SAE J404:2009
Category Alloy Steel Alloy Steel
C (%) 0.17-0.22 0.17-0.22
Cr (%) 0.80-1.20 0.40-0.60
Mn (%) 0.30-0.60 0.45-0.65
Mo (%) 0.30-0.50 0.20-0.30
Ni (%) 3.00-3.50 1.65-2.00
P (%) <=0.025 <=0.030
S (%) <=0.035 <=0.040
Si (%) <=0.40 0.15-0.35
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property EN 10084 20NiCrMo13-4 SAE J404 4320
Condition Soft annealed Not specified
Hardenability +H band at 1.5 mm from the quenched end: 43 to 53 HRC Not specified
Hardness Soft annealed: 255 HB max Not specified
Typical Applications
EN 10084 20NiCrMo13-4
Case hardened machine parts: carburized or carbonitrided, then hardened (clause 3.1)
SAE J404 4320
Used for gears, shafts, aircraft components, pinions, axles, and transmission parts.
Can EN 10084 20NiCrMo13-4 Be Substituted With SAE J404 4320?
EN 10084 20NiCrMo13-4 and SAE J404 4320 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
EN 10084 20NiCrMo13-4
No active listings currently.
SAE J404 4320
Round Bar → (2 listings)
Diameter: 50–50 mm (1.97–1.97 in)
Length: 4600–4600 mm (181.1–181.1 in)
On M-EX Right Now
EN 10084 20NiCrMo13-4
0 active listings and RFQs →
SAE J404 4320
2 active listings and RFQs →
Frequently Asked Questions
What is the difference between EN 10084 20NiCrMo13-4 and SAE J404 4320?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can EN 10084 20NiCrMo13-4 be substituted with SAE J404 4320?
EN 10084 20NiCrMo13-4 and SAE J404 4320 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.