EN 10085 41CrAlMo7 vs IS 1570 (Part 7) 10Cr36Mo10H
Minimal Match — 40.8% match
based on chemical composition and mechanical property overlap.
EN 10085 41CrAlMo7 (EN 10085:2001) and IS 1570 (Part 7) 10Cr36Mo10H (IS 1570 (Part 7):1992) are both steel grades.
Both fall under the Alloy Steel category.
EN 10085 41CrAlMo7 is typically used for nitrided precision components, crankshafts, gears, while IS 1570 (Part 7) 10Cr36Mo10H is commonly used for boilers, pressure vessels, steam turbines, steam and water piping and other power plant equipment working at elevated temperature.
EN 10085 41CrAlMo7 is defined under European Standard (EN), originating from Europe, while IS 1570 (Part 7) 10Cr36Mo10H is defined under Bureau of Indian Standards (IS), originating from India.
As per chemical composition, EN 10085 41CrAlMo7 vs IS 1570 (Part 7) 10Cr36Mo10H is a 61.1% match.
As per mechanical properties, the match is 0%.
Combined, this makes them a minimal match overall at 40.8%.
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
EN 10085 41CrAlMo7
IS 1570 (Part 7) 10Cr36Mo10H
Tensile Strength
850–1000 MPa
410-560 MPa
Surface Hardness HV
≥900 (nitrided)
Not specified
Core Hardness HB
248–302
Not specified
Yield Strength
Not specified
>=135 MPa (0.2 % proof stress)
Elongation
Not specified
>=20%
Condition
Not specified
Pipes, A, thickness - (first row of Table 3)
Typical Applications
EN 10085 41CrAlMo7
Nitrided precision components, crankshafts, gears
IS 1570 (Part 7) 10Cr36Mo10H
Boilers, pressure vessels, steam turbines, steam and water piping and other power plant equipment working at elevated temperature
Key Differences
EN 10085 41CrAlMo7 specifies Al which is not specified for IS 1570 (Part 7) 10Cr36Mo10H.
IS 1570 (Part 7) 10Cr36Mo10H specifies Si, P, S, Al (metallic) which are not specified for EN 10085 41CrAlMo7.
Can EN 10085 41CrAlMo7 Be Substituted With IS 1570 (Part 7) 10Cr36Mo10H?
EN 10085 41CrAlMo7 and IS 1570 (Part 7) 10Cr36Mo10H share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
What is the difference between EN 10085 41CrAlMo7 and IS 1570 (Part 7) 10Cr36Mo10H?
EN 10085 41CrAlMo7 specifies Al which is not specified for IS 1570 (Part 7) 10Cr36Mo10H. IS 1570 (Part 7) 10Cr36Mo10H specifies Si, P, S, Al (metallic) which are not specified for EN 10085 41CrAlMo7.
Can EN 10085 41CrAlMo7 be substituted with IS 1570 (Part 7) 10Cr36Mo10H?
EN 10085 41CrAlMo7 and IS 1570 (Part 7) 10Cr36Mo10H share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.