EN 10088-1 X10CrAlSi7 vs IS 1570 (Part 5) X15Cr25N

Related Material — 69.9% match based on chemical composition and mechanical property overlap.

EN 10088-1 X10CrAlSi7 (EN 10088-1:2014) and IS 1570 (Part 5) X15Cr25N (IS 1570 (Part 5):1985) are both steel grades. Both fall under the Stainless Steel category. EN 10088-1 X10CrAlSi7 is defined under European Standard (EN), originating from Europe, while IS 1570 (Part 5) X15Cr25N is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, EN 10088-1 X10CrAlSi7 vs IS 1570 (Part 5) X15Cr25N is a 74.8% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a related material overall at 69.9%.

Frequently Compared With EN 10088-1 X10CrAlSi7:
ASTM A959 .- GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 GOST 5632 08X18H10 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4401 EN 10088-1 1.4845 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr12Ni2Mo
Match Breakdown
CHEMISTRY MATCH
74.8%
MECHANICAL MATCH
No shared data
OVERALL
69.9%
Specifications
Property EN 10088-1 X10CrAlSi7 IS 1570 (Part 5) X15Cr25N
Standard EN 10088-1:2014 IS 1570 (Part 5):1985
Category Stainless Steel Stainless Steel
C (%) <=0.12 <=0.20
Si (%) 0.50-1.00 <=1.0
Mn (%) <=1.00 <=1.5
P (%) <=0.040 <=0.045
S (%) <=0.015 <=0.030
Cr (%) 6.0-8.0 23.0-27.0
Al (%) 0.50-1.00 Not specified
N (%) Not specified <=0.25
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property EN 10088-1 X10CrAlSi7 IS 1570 (Part 5) X15Cr25N
Tensile Strength Not specified >=515 MPa
Yield Strength Not specified >=275 MPa (0.2 % proof stress)
Elongation Not specified >=20% (50 mm)
Hardness Not specified <=217 HB
Condition Not specified Annealed, quenched or solution treated plates, sheets and strips (Table 2)
Key Differences
Can EN 10088-1 X10CrAlSi7 Be Substituted With IS 1570 (Part 5) X15Cr25N?
EN 10088-1 X10CrAlSi7 and IS 1570 (Part 5) X15Cr25N share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
EN 10088-1 X10CrAlSi7
0 active listings and RFQs →
IS 1570 (Part 5) X15Cr25N
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between EN 10088-1 X10CrAlSi7 and IS 1570 (Part 5) X15Cr25N?
EN 10088-1 X10CrAlSi7 specifies Al which is not specified for IS 1570 (Part 5) X15Cr25N. IS 1570 (Part 5) X15Cr25N specifies N which is not specified for EN 10088-1 X10CrAlSi7.
Can EN 10088-1 X10CrAlSi7 be substituted with IS 1570 (Part 5) X15Cr25N?
EN 10088-1 X10CrAlSi7 and IS 1570 (Part 5) X15Cr25N share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.