EN 10088-1 X1CrNiMoCuN24-22-8 vs ASTM A276/A276M S32654

Strong Match — 95.8% match based on chemical composition and mechanical property overlap.

EN 10088-1 X1CrNiMoCuN24-22-8 (EN 10088-1:2014) and ASTM A276/A276M S32654 (ASTM A276/A276M:2017) are both steel grades. Both fall under the Stainless Steel category. EN 10088-1 X1CrNiMoCuN24-22-8 is defined under European Standard (EN), originating from Europe, while ASTM A276/A276M S32654 is defined under ASTM International, originating from United States.

As per chemical composition, EN 10088-1 X1CrNiMoCuN24-22-8 vs ASTM A276/A276M S32654 is a 95.8% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 95.8%.

Frequently Compared With EN 10088-1 X1CrNiMoCuN24-22-8:
EN 10088-1 1.4845 ASTM A959 .- GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 GOST 5632 08X18H10 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4401 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr12Ni2Mo
Match Breakdown
CHEMISTRY MATCH
95.8%
MECHANICAL MATCH
No shared data
OVERALL
95.8%
Specifications
Property EN 10088-1 X1CrNiMoCuN24-22-8 ASTM A276/A276M S32654
Standard EN 10088-1:2014 ASTM A276/A276M:2017
Category Stainless Steel Stainless Steel
C (%) <=0.020 <=0.020
Si (%) <=0.50 <=0.50
Mn (%) 2.00-4.0 2.0-4.0
P (%) <=0.030 <=0.030
S (%) <=0.005 <=0.005
Cr (%) 23.0-25.0 24.0-25.0
Mo (%) 7.0-8.0 7.0-8.0
Ni (%) 21.0-23.0 21.0-23.0
N (%) 0.45-0.55 0.45-0.55
Cu (%) 0.30-0.60 0.30-0.60
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property EN 10088-1 X1CrNiMoCuN24-22-8 ASTM A276/A276M S32654
Tensile Strength Not specified >=750 MPa
Yield Strength Not specified >=430 MPa
Elongation Not specified >=40%
Hardness Not specified <=250 HB
Condition Not specified Condition A (Annealed), hot-finished or cold-finished, all sizes (first row printed)
Typical Applications
EN 10088-1 X1CrNiMoCuN24-22-8
Not documented
ASTM A276/A276M S32654
Stainless steel bars and shapes (hot-finished or cold-finished)
Can EN 10088-1 X1CrNiMoCuN24-22-8 Be Substituted With ASTM A276/A276M S32654?
EN 10088-1 X1CrNiMoCuN24-22-8 and ASTM A276/A276M S32654 overlap closely enough on chemistry and mechanical properties that ASTM A276/A276M S32654 is often considered as a substitute for EN 10088-1 X1CrNiMoCuN24-22-8 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
EN 10088-1 X1CrNiMoCuN24-22-8
0 active listings and RFQs →
ASTM A276/A276M S32654
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between EN 10088-1 X1CrNiMoCuN24-22-8 and ASTM A276/A276M S32654?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can EN 10088-1 X1CrNiMoCuN24-22-8 be substituted with ASTM A276/A276M S32654?
EN 10088-1 X1CrNiMoCuN24-22-8 and ASTM A276/A276M S32654 overlap closely enough on chemistry and mechanical properties that ASTM A276/A276M S32654 is often considered as a substitute for EN 10088-1 X1CrNiMoCuN24-22-8 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.