EN 10088-1 X6CrNiTi18-10 vs IS 11169 (Part 2) X04Cr18Ni10Ti

Strong Match — 98.6% match based on chemical composition and mechanical property overlap.

EN 10088-1 X6CrNiTi18-10 (EN 10088-1:2014) and IS 11169 (Part 2) X04Cr18Ni10Ti (IS 11169 (Part 2):1989) are both steel grades. Both fall under the Stainless Steel category. EN 10088-1 X6CrNiTi18-10 is defined under European Standard (EN), originating from Europe, while IS 11169 (Part 2) X04Cr18Ni10Ti is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, EN 10088-1 X6CrNiTi18-10 vs IS 11169 (Part 2) X04Cr18Ni10Ti is a 98.6% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 98.6%.

Frequently Compared With EN 10088-1 X6CrNiTi18-10:
EN 10088-1 1.4401 IS 1570 (Part 7) 12Cr12MoVH ASTM A959 .- GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 GOST 5632 08X18H10 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4845 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12Ni2Mo
Match Breakdown
CHEMISTRY MATCH
98.6%
MECHANICAL MATCH
No shared data
OVERALL
98.6%
Specifications
Property EN 10088-1 X6CrNiTi18-10 IS 11169 (Part 2) X04Cr18Ni10Ti
Standard EN 10088-1:2014 IS 11169 (Part 2):1989
Category Stainless Steel Stainless Steel
C (%) <=0.08 <=0.08
Si (%) <=1.00 <=1.0
Mn (%) <=2.00 <=2.0
P (%) <=0.045 <=0.045
S (%) <=0.015 <=0.030
Cr (%) 17.0-19.0 17.0-19.0
Ni (%) 9.0-12.0 9.0-12.0
Ti (%) Not specified >=5xC, <=0.80
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property EN 10088-1 X6CrNiTi18-10 IS 11169 (Part 2) X04Cr18Ni10Ti
Yield Strength (0.2% proof) Not specified >=205 MPa
Tensile Strength Not specified 500-750 MPa
Elongation Not specified >=40%
Impact (U-notch 5 mm) Not specified >=60 J
Condition Not specified Quenched reference test piece (Table 6 treatment)
Typical Applications
EN 10088-1 X6CrNiTi18-10
Not documented
IS 11169 (Part 2) X04Cr18Ni10Ti
Cold heading and cold extrusion; the standard covers wires, wire rods and bars (clause 1.1)
Key Differences
Can EN 10088-1 X6CrNiTi18-10 Be Substituted With IS 11169 (Part 2) X04Cr18Ni10Ti?
EN 10088-1 X6CrNiTi18-10 and IS 11169 (Part 2) X04Cr18Ni10Ti overlap closely enough on chemistry and mechanical properties that IS 11169 (Part 2) X04Cr18Ni10Ti is often considered as a substitute for EN 10088-1 X6CrNiTi18-10 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
EN 10088-1 X6CrNiTi18-10
0 active listings and RFQs →
IS 11169 (Part 2) X04Cr18Ni10Ti
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between EN 10088-1 X6CrNiTi18-10 and IS 11169 (Part 2) X04Cr18Ni10Ti?
IS 11169 (Part 2) X04Cr18Ni10Ti specifies Ti which is not specified for EN 10088-1 X6CrNiTi18-10.
Can EN 10088-1 X6CrNiTi18-10 be substituted with IS 11169 (Part 2) X04Cr18Ni10Ti?
EN 10088-1 X6CrNiTi18-10 and IS 11169 (Part 2) X04Cr18Ni10Ti overlap closely enough on chemistry and mechanical properties that IS 11169 (Part 2) X04Cr18Ni10Ti is often considered as a substitute for EN 10088-1 X6CrNiTi18-10 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.