EN 10088-1 X1NiCrMoCu25-20-5 vs IS 6603 X01Ni25Cr20Mo5Cu
Strong Match — 93.9% match
based on chemical composition and mechanical property overlap.
EN 10088-1 X1NiCrMoCu25-20-5 (EN 10088-1:2023) and IS 6603 X01Ni25Cr20Mo5Cu (IS 6603:2024) are both steel grades.
Both fall under the Stainless Steel category.
EN 10088-1 X1NiCrMoCu25-20-5 is defined under European Standard (EN), originating from Europe, while IS 6603 X01Ni25Cr20Mo5Cu is defined under Bureau of Indian Standards (IS), originating from India.
As per chemical composition, EN 10088-1 X1NiCrMoCu25-20-5 vs IS 6603 X01Ni25Cr20Mo5Cu is a 93.9% match.
Mechanical property data is not available for both grades, so this factor could not be scored.
Combined, this makes them a strong match overall at 93.9%.
Frequently Compared With EN 10088-1 X1NiCrMoCu25-20-5:
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
EN 10088-1 X1NiCrMoCu25-20-5
IS 6603 X01Ni25Cr20Mo5Cu
Tensile Strength
Not specified
530-730 MPa
Yield Strength
Not specified
>=220 MPa
Elongation
Not specified
>=35%
Condition
Not specified
Solution annealed, conditions 1C, 1E, 1D, 1X, 1G and 2D, thickness or diameter up to 160 mm; Yield Strength is Rp0.2, Elongation is A (longitudinal)
Typical Applications
EN 10088-1 X1NiCrMoCu25-20-5
Not documented
IS 6603 X01Ni25Cr20Mo5Cu
General purposes, semi-finished products, bars, wire rods and bright bars
Can EN 10088-1 X1NiCrMoCu25-20-5 Be Substituted With IS 6603 X01Ni25Cr20Mo5Cu?
EN 10088-1 X1NiCrMoCu25-20-5 and IS 6603 X01Ni25Cr20Mo5Cu overlap closely enough on chemistry and mechanical properties that IS 6603 X01Ni25Cr20Mo5Cu is often considered as a substitute for EN 10088-1 X1NiCrMoCu25-20-5 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
What is the difference between EN 10088-1 X1NiCrMoCu25-20-5 and IS 6603 X01Ni25Cr20Mo5Cu?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can EN 10088-1 X1NiCrMoCu25-20-5 be substituted with IS 6603 X01Ni25Cr20Mo5Cu?
EN 10088-1 X1NiCrMoCu25-20-5 and IS 6603 X01Ni25Cr20Mo5Cu overlap closely enough on chemistry and mechanical properties that IS 6603 X01Ni25Cr20Mo5Cu is often considered as a substitute for EN 10088-1 X1NiCrMoCu25-20-5 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.