Close Alternative — 74.9% match
based on chemical composition and mechanical property overlap.
EN 10088-1 X3CrNiCu18-9-4 (EN 10088-1:2023) and EN 10088-1 1.4301 (EN 10088-1:2014) are both steel grades.
Both fall under the Stainless Steel category.
EN 10088-1 X3CrNiCu18-9-4 is defined under European Standard (EN), originating from Europe, while EN 10088-1 1.4301 is defined under European Standard (EN), originating from Europe.
As per chemical composition, EN 10088-1 X3CrNiCu18-9-4 vs EN 10088-1 1.4301 is a 74.9% match.
Mechanical property data is not available for both grades, so this factor could not be scored.
Combined, this makes them a close alternative overall at 74.9%.
Frequently Compared With EN 10088-1 X3CrNiCu18-9-4:
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
EN 10088-1 X3CrNiCu18-9-4
EN 10088-1 1.4301
Tensile Strength
Not specified
≥520 MPa
Yield Strength
Not specified
≥210 MPa
Elongation
Not specified
≥45%
Hardness
Not specified
≤215 HB
Typical Applications
EN 10088-1 X3CrNiCu18-9-4
Not documented
EN 10088-1 1.4301
Food equipment, chemical vessels, architectural, kitchenware
Key Differences
EN 10088-1 X3CrNiCu18-9-4 specifies N, Cu which are not specified for EN 10088-1 1.4301.
Can EN 10088-1 X3CrNiCu18-9-4 Be Substituted With EN 10088-1 1.4301?
EN 10088-1 X3CrNiCu18-9-4 and EN 10088-1 1.4301 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
What is the difference between EN 10088-1 X3CrNiCu18-9-4 and EN 10088-1 1.4301?
EN 10088-1 X3CrNiCu18-9-4 specifies N, Cu which are not specified for EN 10088-1 1.4301.
Can EN 10088-1 X3CrNiCu18-9-4 be substituted with EN 10088-1 1.4301?
EN 10088-1 X3CrNiCu18-9-4 and EN 10088-1 1.4301 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.