EN 10088-1 X3CrNiCuMo17-11-3-2 vs IS 11169 (Part 2) X02Cr17Ni11Cu3Mo2

Strong Match — 100% match based on chemical composition and mechanical property overlap.

EN 10088-1 X3CrNiCuMo17-11-3-2 (EN 10088-1:2023) and IS 11169 (Part 2) X02Cr17Ni11Cu3Mo2 (IS 11169 (Part 2):2023) are both steel grades. Both fall under the Stainless Steel category. EN 10088-1 X3CrNiCuMo17-11-3-2 is defined under European Standard (EN), originating from Europe, while IS 11169 (Part 2) X02Cr17Ni11Cu3Mo2 is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, EN 10088-1 X3CrNiCuMo17-11-3-2 vs IS 11169 (Part 2) X02Cr17Ni11Cu3Mo2 is a 100% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 100%.

Frequently Compared With EN 10088-1 X3CrNiCuMo17-11-3-2:
GOST 5632 06Kh23N28 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4401 EN 10088-1 1.4845 ASTM A959 .- GB/T 3280 06Cr19Ni10 GOST 5632 08X18H10 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr12Ni2Mo
Match Breakdown
CHEMISTRY MATCH
100%
MECHANICAL MATCH
No shared data
OVERALL
100%
Specifications
Property EN 10088-1 X3CrNiCuMo17-11-3-2 IS 11169 (Part 2) X02Cr17Ni11Cu3Mo2
Standard EN 10088-1:2023 IS 11169 (Part 2):2023
Category Stainless Steel Stainless Steel
C (%) <=0.04 <=0.04
Si (%) <=1.00 <=1.00
Mn (%) <=2.00 <=2.00
P (%) <=0.045 <=0.045
S (%) <=0.015 <=0.015
Cr (%) 16.5-17.5 16.5-17.5
Mo (%) 2.00-2.50 2.00-2.50
Ni (%) 10.0-11.0 10.0-11.0
N (%) <=0.10 <=0.10
Cu (%) 3.0-3.5 3.00-3.50
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property EN 10088-1 X3CrNiCuMo17-11-3-2 IS 11169 (Part 2) X02Cr17Ni11Cu3Mo2
Reduction of Area, solution annealed (+AT) Not specified >=68% (over 5 to 50 mm)
Tensile Strength, solution annealed (+AT) Not specified <=610 MPa (over 5 to 50 mm)
Typical Applications
EN 10088-1 X3CrNiCuMo17-11-3-2
Not documented
IS 11169 (Part 2) X02Cr17Ni11Cu3Mo2
Cold heading and cold extrusion of stainless steel parts; the standard covers wires, wire rods and bars of 0.8 to 50 mm (clause 1.1, Table 11)
Can EN 10088-1 X3CrNiCuMo17-11-3-2 Be Substituted With IS 11169 (Part 2) X02Cr17Ni11Cu3Mo2?
EN 10088-1 X3CrNiCuMo17-11-3-2 and IS 11169 (Part 2) X02Cr17Ni11Cu3Mo2 overlap closely enough on chemistry and mechanical properties that IS 11169 (Part 2) X02Cr17Ni11Cu3Mo2 is often considered as a substitute for EN 10088-1 X3CrNiCuMo17-11-3-2 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
EN 10088-1 X3CrNiCuMo17-11-3-2
0 active listings and RFQs →
IS 11169 (Part 2) X02Cr17Ni11Cu3Mo2
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between EN 10088-1 X3CrNiCuMo17-11-3-2 and IS 11169 (Part 2) X02Cr17Ni11Cu3Mo2?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can EN 10088-1 X3CrNiCuMo17-11-3-2 be substituted with IS 11169 (Part 2) X02Cr17Ni11Cu3Mo2?
EN 10088-1 X3CrNiCuMo17-11-3-2 and IS 11169 (Part 2) X02Cr17Ni11Cu3Mo2 overlap closely enough on chemistry and mechanical properties that IS 11169 (Part 2) X02Cr17Ni11Cu3Mo2 is often considered as a substitute for EN 10088-1 X3CrNiCuMo17-11-3-2 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.