IS 11169 (Part 2):2023 X02Cr17Ni11Cu3Mo2 Steel: Specifications & Listings

IS 11169 (Part 2):2023 X02Cr17Ni11Cu3Mo2: Cold heading quality austenitic stainless steel with molybdenum X02Cr17Ni11Cu3Mo2 to IS 11169 (Part 2):2023, supplied as wire rod, bars or wire of 0.8 to 50 mm. Maximum tensile strength solution annealed is 610 MPa.

Category: Stainless Steel
Grade Details
GradeIS 11169 (Part 2):2023 X02Cr17Ni11Cu3Mo2
Standard IS 11169 (Part 2):2023
ApplicationsCold heading and cold extrusion of stainless steel parts; the standard covers wires, wire rods and bars of 0.8 to 50 mm (clause 1.1, Table 11)
Equivalent / Similar Grades
Grade Standard Region Live on M-EX
ISO 4578-316-76-E ISO 4954 International Not yet on M-EX
EN X3CrNiCuMo17-11-3-2 (1.4578) EN 10263 Europe Not yet on M-EX
EN 10088-1 X3CrNiCuMo17-11-3-2 EN 10088-1:2014 Europe (CEN) No activity yet
Grade ComparisonCompare With a Specific Grade →
Grade Standard Match
EN 10088-1 X3CrNiCuMo17-11-3-2 EN 10088-1:2014 Strong Match
EN 10088-1 X3CrNiCuMo17-11-3-2 EN 10088-1:2023 Strong Match
EN 10088-1 X2CrNiMo17-12-2 EN 10088-1:2014 Strong Match
EN 10088-1 X2CrNiMoCuS17-10-2 EN 10088-1:2014 Close Alternative
EN 10088-1 X2CrNiMoCuS17-10-2 EN 10088-1:2023 Close Alternative
EN 10088-1 X2CrNiMo17-12-2 EN 10088-1:2023 Close Alternative
EN 10088-1 X2CrNiMoN17-11-2 EN 10088-1:2014 Close Alternative
EN 10088-1 X2CrNiMoN17-11-2 EN 10088-1:2023 Close Alternative
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Chemical Composition (%)
C Cr Cu Mn Mo N Ni P S Si
<=0.04 16.5-17.5 3.00-3.50 <=2.00 2.00-2.50 <=0.10 10.0-11.0 <=0.045 <=0.015 <=1.00
Mechanical Properties
Reduction of Area, solution annealed (+AT) >=68% (over 5 to 50 mm)
Tensile Strength, solution annealed (+AT) <=610 MPa (over 5 to 50 mm)

More data from IS 11169 (Part 2):2023

From the standard
Other composition limits from the table notes
Values
Maximum unless a range is given (ladle analysis)
Steel type
Austenitic with molybdenum
Elements not listed are not added intentionally without the purchaser's agreement, except those used to finish the heat.
Source: IS 11169 (Part 2):2023, Table 10 and its notes
Tensile strength and reduction of area by delivery condition by delivery condition and size
Delivery conditionDiameter (mm)Tensile strength, max (MPa)Reduction of area, min (%)
+AT or +AT+PEover 5 to 1061068
+AT or +AT+PEover 10 to 2561068
+AT or +AT+PEover 25 to 5061068
+AT+Cover 5 to 10760-
+AT+Cover 10 to 25720-
+AT+C+ATover 2 to 563068
+AT+C+ATover 5 to 1061068
+AT+C+ATover 10 to 2561068
+AT+C+AT+LCover 2 to 568063
+AT+C+AT+LCover 5 to 1066063
Codes: +AT solution annealed, +A soft annealed, +PE peeled, +C cold drawn, +LC skin passed. Diameter ranges are over the first figure up to and including the second. No reduction of area is specified for +AT+C. For non-circular sections the properties are agreed between manufacturer and purchaser.
Source: IS 11169 (Part 2):2023, Table 11

Active IS 11169 (Part 2):2023 X02Cr17Ni11Cu3Mo2 Listings on M-EX (For Sale)

+ Create a Listing for this grade

No active IS 11169 (Part 2):2023 X02Cr17Ni11Cu3Mo2 listings at this time.

Register for Alerts

Buyer RFQs for IS 11169 (Part 2):2023 X02Cr17Ni11Cu3Mo2

+ Post an RFQ for this grade

No open buyer requirements for IS 11169 (Part 2):2023 X02Cr17Ni11Cu3Mo2 at this time.

Register for Alerts