Strong Match — 95.5% match
based on chemical composition and mechanical property overlap.
EN 10088-1 X6Cr17 (EN 10088-1:2023) and IS 11169 (Part 2) X07Cr17 (IS 11169 (Part 2):1989) are both steel grades.
Both fall under the Stainless Steel category.
EN 10088-1 X6Cr17 is defined under European Standard (EN), originating from Europe, while IS 11169 (Part 2) X07Cr17 is defined under Bureau of Indian Standards (IS), originating from India.
As per chemical composition, EN 10088-1 X6Cr17 vs IS 11169 (Part 2) X07Cr17 is a 95.5% match.
Mechanical property data is not available for both grades, so this factor could not be scored.
Combined, this makes them a strong match overall at 95.5%.
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
EN 10088-1 X6Cr17
IS 11169 (Part 2) X07Cr17
Yield Strength (0.2% proof)
Not specified
>=270 MPa
Tensile Strength
Not specified
450-600 MPa
Elongation
Not specified
>=20%
Condition
Not specified
Annealed reference test piece (Table 6 treatment)
Typical Applications
EN 10088-1 X6Cr17
Not documented
IS 11169 (Part 2) X07Cr17
Cold heading and cold extrusion; the standard covers wires, wire rods and bars (clause 1.1)
Can EN 10088-1 X6Cr17 Be Substituted With IS 11169 (Part 2) X07Cr17?
EN 10088-1 X6Cr17 and IS 11169 (Part 2) X07Cr17 overlap closely enough on chemistry and mechanical properties that IS 11169 (Part 2) X07Cr17 is often considered as a substitute for EN 10088-1 X6Cr17 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
What is the difference between EN 10088-1 X6Cr17 and IS 11169 (Part 2) X07Cr17?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can EN 10088-1 X6Cr17 be substituted with IS 11169 (Part 2) X07Cr17?
EN 10088-1 X6Cr17 and IS 11169 (Part 2) X07Cr17 overlap closely enough on chemistry and mechanical properties that IS 11169 (Part 2) X07Cr17 is often considered as a substitute for EN 10088-1 X6Cr17 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.