Post Stock Login Register

EN 10088-1 X6CrNi18-10 vs NF A35-574 Z7CN18-09

Strong Match — 89.7% match based on chemical composition and mechanical property overlap.

EN 10088-1 X6CrNi18-10 (EN 10088-1:2023) and NF A35-574 Z7CN18-09 (NF A35-574:1990) are both steel grades. Both fall under the Stainless Steel category. EN 10088-1 X6CrNi18-10 is defined under European Standard (EN), originating from Europe, while NF A35-574 Z7CN18-09 is defined under Association Francaise de Normalisation (NF), originating from France.

As per chemical composition, EN 10088-1 X6CrNi18-10 vs NF A35-574 Z7CN18-09 is a 89.7% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 89.7%.

Frequently Compared With EN 10088-1 X6CrNi18-10:
GOST 5632 06Kh23N28 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4401 EN 10088-1 1.4845 ASTM A959 .- GB/T 3280 06Cr19Ni10 GOST 5632 08X18H10 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr12Ni2Mo
Match Breakdown
CHEMISTRY MATCH
89.7%
MECHANICAL MATCH
No shared data
OVERALL
89.7%
Specifications
Property EN 10088-1 X6CrNi18-10 NF A35-574 Z7CN18-09
Standard EN 10088-1:2023 NF A35-574:1990
Category Stainless Steel Stainless Steel
C (%) 0.04-0.08 0.08 max
Si (%) <=1.00 1.00 max
Mn (%) <=2.00 2.00 max
P (%) <=0.035 0.045 max
S (%) <=0.015 0.030 max
Cr (%) 17.0-19.0 17.00-19.00
Ni (%) 8.0-11.0 8.00-10.50
N (%) <=0.10 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property EN 10088-1 X6CrNi18-10 NF A35-574 Z7CN18-09
Tensile Strength Not specified 500-700 MPa
Yield Strength Not specified 190-250 MPa
Elongation Not specified 40-55%
Hardness Not specified 140-210 HB
Typical Applications
EN 10088-1 X6CrNi18-10
Not documented
NF A35-574 Z7CN18-09
Used for food processing equipment, kitchen equipment, chemical tanks, piping, architectural components, and fasteners.
Key Differences
Can EN 10088-1 X6CrNi18-10 Be Substituted With NF A35-574 Z7CN18-09?
EN 10088-1 X6CrNi18-10 and NF A35-574 Z7CN18-09 overlap closely enough on chemistry and mechanical properties that NF A35-574 Z7CN18-09 is often considered as a substitute for EN 10088-1 X6CrNi18-10 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
Forms & Sizes Available on M-EX
EN 10088-1 X6CrNi18-10
No active listings currently.
NF A35-574 Z7CN18-09
Sheet → (2 listings)
Thickness: 6–6 mm (0.24–0.24 in)
Width: 1250–1250 mm (49.21–49.21 in)
Length: 2600–2900 mm (102.36–114.17 in)
On M-EX Right Now
EN 10088-1 X6CrNi18-10
0 active listings and RFQs →
NF A35-574 Z7CN18-09
2 active listings and RFQs →
Frequently Asked Questions
What is the difference between EN 10088-1 X6CrNi18-10 and NF A35-574 Z7CN18-09?
EN 10088-1 X6CrNi18-10 specifies N which is not specified for NF A35-574 Z7CN18-09.
Can EN 10088-1 X6CrNi18-10 be substituted with NF A35-574 Z7CN18-09?
EN 10088-1 X6CrNi18-10 and NF A35-574 Z7CN18-09 overlap closely enough on chemistry and mechanical properties that NF A35-574 Z7CN18-09 is often considered as a substitute for EN 10088-1 X6CrNi18-10 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.