EN 10088-1 X5CrNi18-10 vs IS 11169 (Part 2) X04Cr19Ni10
Strong Match — 96% match
based on chemical composition and mechanical property overlap.
EN 10088-1 X5CrNi18-10 (EN 10088-1:2014) and IS 11169 (Part 2) X04Cr19Ni10 (IS 11169 (Part 2):2023) are both steel grades.
Both fall under the Stainless Steel category.
EN 10088-1 X5CrNi18-10 is typically used for food, chemical, architectural applications, while IS 11169 (Part 2) X04Cr19Ni10 is commonly used for cold heading and cold extrusion of stainless steel parts; the standard covers wires, wire rods and bars of 0.8 to 50 mm (clause 1.1, table 11).
EN 10088-1 X5CrNi18-10 is defined under European Standard (EN), originating from Europe, while IS 11169 (Part 2) X04Cr19Ni10 is defined under Bureau of Indian Standards (IS), originating from India.
As per chemical composition, EN 10088-1 X5CrNi18-10 vs IS 11169 (Part 2) X04Cr19Ni10 is a 96% match.
Mechanical property data is not available for both grades, so this factor could not be scored.
Combined, this makes them a strong match overall at 96%.
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
EN 10088-1 X5CrNi18-10
IS 11169 (Part 2) X04Cr19Ni10
Reduction of Area, solution annealed (+AT)
Not specified
>=65% (over 5 to 50 mm)
Tensile Strength, solution annealed (+AT)
Not specified
<=650 MPa (over 5 to 50 mm)
Typical Applications
EN 10088-1 X5CrNi18-10
Food, chemical, architectural applications
IS 11169 (Part 2) X04Cr19Ni10
Cold heading and cold extrusion of stainless steel parts; the standard covers wires, wire rods and bars of 0.8 to 50 mm (clause 1.1, Table 11)
Key Differences
IS 11169 (Part 2) X04Cr19Ni10 specifies Cu which is not specified for EN 10088-1 X5CrNi18-10.
Can EN 10088-1 X5CrNi18-10 Be Substituted With IS 11169 (Part 2) X04Cr19Ni10?
EN 10088-1 X5CrNi18-10 and IS 11169 (Part 2) X04Cr19Ni10 overlap closely enough on chemistry and mechanical properties that IS 11169 (Part 2) X04Cr19Ni10 is often considered as a substitute for EN 10088-1 X5CrNi18-10 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
What is the difference between EN 10088-1 X5CrNi18-10 and IS 11169 (Part 2) X04Cr19Ni10?
IS 11169 (Part 2) X04Cr19Ni10 specifies Cu which is not specified for EN 10088-1 X5CrNi18-10.
Can EN 10088-1 X5CrNi18-10 be substituted with IS 11169 (Part 2) X04Cr19Ni10?
EN 10088-1 X5CrNi18-10 and IS 11169 (Part 2) X04Cr19Ni10 overlap closely enough on chemistry and mechanical properties that IS 11169 (Part 2) X04Cr19Ni10 is often considered as a substitute for EN 10088-1 X5CrNi18-10 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.