EN 10088-2 X1CrNiMoCu12-7-3 vs EN 10088-2 X1CrNiMoCu12-5-2

Related Material — 69.9% match based on chemical composition and mechanical property overlap.

EN 10088-2 X1CrNiMoCu12-7-3 (EN 10088-2:2014) and EN 10088-2 X1CrNiMoCu12-5-2 (EN 10088-2:2014) are both steel grades. Both fall under the Stainless Steel category. EN 10088-2 X1CrNiMoCu12-7-3 is typically used for general purposes, hot or cold rolled sheet/plate and strip, while EN 10088-2 X1CrNiMoCu12-5-2 is commonly used for general purposes, hot or cold rolled sheet/plate and strip. EN 10088-2 X1CrNiMoCu12-7-3 is defined under European Standard (EN), originating from Europe, while EN 10088-2 X1CrNiMoCu12-5-2 is defined under European Standard (EN), originating from Europe.

As per chemical composition, EN 10088-2 X1CrNiMoCu12-7-3 vs EN 10088-2 X1CrNiMoCu12-5-2 is a 83.3% match. As per mechanical properties, the match is 100%. Combined, this makes them a related material overall at 69.9%.

Frequently Compared With EN 10088-2 X1CrNiMoCu12-7-3:
ASTM A959 .- GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 GOST 5632 08X18H10 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4401 EN 10088-1 1.4845 IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr12Ni2Mo IS 1570 (Part 7) 11Cr17Ni13W3TiH
Match Breakdown
CHEMISTRY MATCH
83.3%
MECHANICAL MATCH
100%
OVERALL
69.9%
Specifications
Property EN 10088-2 X1CrNiMoCu12-7-3 EN 10088-2 X1CrNiMoCu12-5-2
Standard EN 10088-2:2014 EN 10088-2:2014
Category Stainless Steel Stainless Steel
C (%) <=0.020 <=0.020
Si (%) <=0.50 <=0.50
Mn (%) <=2.00 <=2.00
P (%) <=0.040 <=0.040
S (%) <=0.003 <=0.003
Cr (%) 11.0-13.0 11.0-13.0
Mo (%) 2.30-2.80 1.30-1.80
Ni (%) 6.0-7.0 4.0-5.0
Cu (%) 0.20-0.80 0.20-0.80
N (%) <=0.020 <=0.020
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property EN 10088-2 X1CrNiMoCu12-7-3 EN 10088-2 X1CrNiMoCu12-5-2
Tensile Strength 750-950 MPa 750-950 MPa
Yield Strength >=550 MPa >=550 MPa
Elongation >=15% >=15%
Hardness <=300 HB <=300 HB
Condition Annealed (+A), hot rolled strip, up to 13.5 mm thick Annealed (+A), hot rolled strip, up to 13.5 mm thick
Typical Applications
EN 10088-2 X1CrNiMoCu12-7-3
General purposes, hot or cold rolled sheet/plate and strip
EN 10088-2 X1CrNiMoCu12-5-2
General purposes, hot or cold rolled sheet/plate and strip
Can EN 10088-2 X1CrNiMoCu12-7-3 Be Substituted With EN 10088-2 X1CrNiMoCu12-5-2?
EN 10088-2 X1CrNiMoCu12-7-3 and EN 10088-2 X1CrNiMoCu12-5-2 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
EN 10088-2 X1CrNiMoCu12-7-3
0 active listings and RFQs →
EN 10088-2 X1CrNiMoCu12-5-2
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between EN 10088-2 X1CrNiMoCu12-7-3 and EN 10088-2 X1CrNiMoCu12-5-2?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can EN 10088-2 X1CrNiMoCu12-7-3 be substituted with EN 10088-2 X1CrNiMoCu12-5-2?
EN 10088-2 X1CrNiMoCu12-7-3 and EN 10088-2 X1CrNiMoCu12-5-2 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.