EN 10088-2 X1CrNiMoCuN24-22-8 vs ASTM A276/A276M S32654
Strong Match — 86.1% match
based on chemical composition and mechanical property overlap.
EN 10088-2 X1CrNiMoCuN24-22-8 (EN 10088-2:2014) and ASTM A276/A276M S32654 (ASTM A276/A276M:2017) are both steel grades.
Both fall under the Stainless Steel category.
EN 10088-2 X1CrNiMoCuN24-22-8 is typically used for general purposes, hot or cold rolled sheet/plate and strip, while ASTM A276/A276M S32654 is commonly used for stainless steel bars and shapes (hot-finished or cold-finished).
EN 10088-2 X1CrNiMoCuN24-22-8 is defined under European Standard (EN), originating from Europe, while ASTM A276/A276M S32654 is defined under ASTM International, originating from United States.
As per chemical composition, EN 10088-2 X1CrNiMoCuN24-22-8 vs ASTM A276/A276M S32654 is a 95.8% match.
As per mechanical properties, the match is 66.7%.
Combined, this makes them a strong match overall at 86.1%.
Frequently Compared With EN 10088-2 X1CrNiMoCuN24-22-8:
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
EN 10088-2 X1CrNiMoCuN24-22-8
ASTM A276/A276M S32654
Tensile Strength
750-1000 MPa
>=750 MPa
Yield Strength
>=430 MPa
>=430 MPa
Elongation
>=40%
>=40%
Condition
Solution annealed (+AT), cold rolled strip, up to 8 mm thick; Yield Strength is Rp0.2 (transverse), Elongation is A80 for under 3 mm thick
Condition A (Annealed), hot-finished or cold-finished, all sizes (first row printed)
Hardness
Not specified
<=250 HB
Typical Applications
EN 10088-2 X1CrNiMoCuN24-22-8
General purposes, hot or cold rolled sheet/plate and strip
ASTM A276/A276M S32654
Stainless steel bars and shapes (hot-finished or cold-finished)
Can EN 10088-2 X1CrNiMoCuN24-22-8 Be Substituted With ASTM A276/A276M S32654?
EN 10088-2 X1CrNiMoCuN24-22-8 and ASTM A276/A276M S32654 overlap closely enough on chemistry and mechanical properties that ASTM A276/A276M S32654 is often considered as a substitute for EN 10088-2 X1CrNiMoCuN24-22-8 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
What is the difference between EN 10088-2 X1CrNiMoCuN24-22-8 and ASTM A276/A276M S32654?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can EN 10088-2 X1CrNiMoCuN24-22-8 be substituted with ASTM A276/A276M S32654?
EN 10088-2 X1CrNiMoCuN24-22-8 and ASTM A276/A276M S32654 overlap closely enough on chemistry and mechanical properties that ASTM A276/A276M S32654 is often considered as a substitute for EN 10088-2 X1CrNiMoCuN24-22-8 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.