EN 10088-2:2014 X1CrNiMoCuNW24-22-6 Steel: Specifications & Listings

EN 10088-2:2014 X1CrNiMoCuNW24-22-6: X1CrNiMoCuNW24-22-6: austenitic corrosion resisting stainless steel, material number 1.4659. Specified in EN 10088-2:2014.

Category: Stainless Steel
Grade Details
GradeEN 10088-2:2014 X1CrNiMoCuNW24-22-6
Standard EN 10088-2:2014
ApplicationsGeneral purposes, hot or cold rolled sheet/plate and strip
Equivalent / Similar Grades
Grade Standard Region Live on M-EX
IS 6603 X01Cr24Ni22Mo4CuNW IS 6603:2024 India No activity yet
EN 10088-1 X1CrNiMoCuNW24-22-6 EN 10088-1:2014 Europe (CEN) No activity yet
EN 10088-3 X1CrNiMoCuNW24-22-6 EN 10088-3:2014 Europe No activity yet
Grade ComparisonCompare With a Specific Grade →
Grade Standard Match
EN 10088-1 X1CrNiMoCuNW24-22-6 EN 10088-1:2014 Strong Match
EN 10088-1 X1CrNiMoCuNW24-22-6 EN 10088-1:2023 Strong Match
IS 6603 X01Cr24Ni22Mo4CuNW IS 6603:2024 Strong Match
EN 10088-3 X1CrNiMoCuNW24-22-6 EN 10088-3:2014 Strong Match
ASTM A959 S31266 ASTM A959:2011 Close Alternative
ASTM A959 S32654 ASTM A959:2011 Related Material
EN 10088-1 X1CrNiMoCuN24-22-8 EN 10088-1:2014 Related Material
EN 10088-1 X1CrNiMoCuN24-22-8 EN 10088-1:2023 Related Material
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Chemical Composition (%)
C Si Mn P S Cr Mo Ni N Cu W
<=0.020 <=0.70 2.00-4.0 <=0.030 <=0.010 23.0-25.0 5.5-6.5 21.0-23.0 0.35-0.50 1.00-2.00 1.50-2.50
Mechanical Properties
Tensile Strength 800-1000 MPa
Yield Strength >=420 MPa
Elongation >=40%
Condition Solution annealed (+AT), hot rolled plate, up to 75 mm thick; Yield Strength is Rp0.2 (transverse), Elongation is A for 3 mm and over

More data from EN 10088-2:2014

From the standard
Mechanical properties by product form and thickness 1 product form
Product formMax thickness (mm)Rp0.2 min (MPa)Rp1.0 min (MPa)Rm (MPa)A80 min, under 3 mm thick (%)A min, 3 mm and over (%)
Hot rolled plate75420460800 to 1000-40
Solution annealed condition; proof strength and elongation are minimum transverse values.
Source: EN 10088-2:2014, Table 7
Impact energy KV2 (ISO-V) 1 rows
Product formMax thickness (mm)KV2 longitudinal, min (J)KV2 transverse, min (J)
Hot rolled plate7510060
Applies to products more than 10 mm thick, ISO-V notch, room temperature.
Source: EN 10088-2:2014, Table 7
Proof strength at elevated temperature 10 temperatures
Temperature (deg C)Rp0.2 min (MPa)Rp1.0 min (MPa)
100350390
150330365
200315350
250307342
300300335
350298328
400295325
450288318
500280310
550270300
Minimum values, solution annealed (+AT).
Source: EN 10088-2:2014, Table 12
Hot forming and solution annealing guideline temperatures
Hot forming temperature
1150 to 850 deg C
Cooling after hot forming
air
Heat treatment symbol
+AT
Solution annealing temperature
1140 to 1200 deg C
Cooling after solution annealing
water, air
Informative guideline; cooling must be rapid enough to avoid intergranular corrosion.
Source: EN 10088-2:2014, Table A.1

Active EN 10088-2:2014 X1CrNiMoCuNW24-22-6 Listings on M-EX (For Sale)

+ Create a Listing for this grade

No active EN 10088-2:2014 X1CrNiMoCuNW24-22-6 listings at this time.

Register for Alerts

Buyer RFQs for EN 10088-2:2014 X1CrNiMoCuNW24-22-6

+ Post an RFQ for this grade

No open buyer requirements for EN 10088-2:2014 X1CrNiMoCuNW24-22-6 at this time.

Register for Alerts