EN 10088-2 X1CrNiMoCuNW24-22-6 vs EN 10088-1 X1CrNiMoCuN24-22-8

Related Material — 69.9% match based on chemical composition and mechanical property overlap.

EN 10088-2 X1CrNiMoCuNW24-22-6 (EN 10088-2:2014) and EN 10088-1 X1CrNiMoCuN24-22-8 (EN 10088-1:2023) are both steel grades. Both fall under the Stainless Steel category. EN 10088-2 X1CrNiMoCuNW24-22-6 is defined under European Standard (EN), originating from Europe, while EN 10088-1 X1CrNiMoCuN24-22-8 is defined under European Standard (EN), originating from Europe.

As per chemical composition, EN 10088-2 X1CrNiMoCuNW24-22-6 vs EN 10088-1 X1CrNiMoCuN24-22-8 is a 76.2% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a related material overall at 69.9%.

Frequently Compared With EN 10088-2 X1CrNiMoCuNW24-22-6:
EN 10088-1 1.4845 ASTM A959 .- GOST 5632 06Kh23N28 GOST 5632 08X18H10 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4401 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr12Ni2Mo IS 1570 (Part 7) 12Cr13H
Match Breakdown
CHEMISTRY MATCH
76.2%
MECHANICAL MATCH
No shared data
OVERALL
69.9%
Specifications
Property EN 10088-2 X1CrNiMoCuNW24-22-6 EN 10088-1 X1CrNiMoCuN24-22-8
Standard EN 10088-2:2014 EN 10088-1:2023
Category Stainless Steel Stainless Steel
C (%) <=0.020 <=0.020
Si (%) <=0.70 <=0.50
Mn (%) 2.00-4.0 2.00-4.0
P (%) <=0.030 <=0.030
S (%) <=0.010 <=0.005
Cr (%) 23.0-25.0 23.0-25.0
Mo (%) 5.5-6.5 7.0-8.0
Ni (%) 21.0-23.0 21.0-23.0
N (%) 0.35-0.50 0.45-0.55
Cu (%) 1.00-2.00 0.30-0.60
W (%) 1.50-2.50 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property EN 10088-2 X1CrNiMoCuNW24-22-6 EN 10088-1 X1CrNiMoCuN24-22-8
Tensile Strength 800-1000 MPa Not specified
Yield Strength >=420 MPa Not specified
Elongation >=40% Not specified
Condition Solution annealed (+AT), hot rolled plate, up to 75 mm thick; Yield Strength is Rp0.2 (transverse), Elongation is A for 3 mm and over Not specified
Typical Applications
EN 10088-2 X1CrNiMoCuNW24-22-6
General purposes, hot or cold rolled sheet/plate and strip
EN 10088-1 X1CrNiMoCuN24-22-8
Not documented
Key Differences
Can EN 10088-2 X1CrNiMoCuNW24-22-6 Be Substituted With EN 10088-1 X1CrNiMoCuN24-22-8?
EN 10088-2 X1CrNiMoCuNW24-22-6 and EN 10088-1 X1CrNiMoCuN24-22-8 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
EN 10088-2 X1CrNiMoCuNW24-22-6
0 active listings and RFQs →
EN 10088-1 X1CrNiMoCuN24-22-8
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between EN 10088-2 X1CrNiMoCuNW24-22-6 and EN 10088-1 X1CrNiMoCuN24-22-8?
EN 10088-2 X1CrNiMoCuNW24-22-6 specifies W which is not specified for EN 10088-1 X1CrNiMoCuN24-22-8.
Can EN 10088-2 X1CrNiMoCuNW24-22-6 be substituted with EN 10088-1 X1CrNiMoCuN24-22-8?
EN 10088-2 X1CrNiMoCuNW24-22-6 and EN 10088-1 X1CrNiMoCuN24-22-8 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.