EN 10088-2 X1NiCrMoCu25-20-5 vs IS 6603 X01Ni25Cr20Mo5Cu
Close Alternative — 84.8% match
based on chemical composition and mechanical property overlap.
EN 10088-2 X1NiCrMoCu25-20-5 (EN 10088-2:2014) and IS 6603 X01Ni25Cr20Mo5Cu (IS 6603:2024) are both steel grades.
Both fall under the Stainless Steel category.
EN 10088-2 X1NiCrMoCu25-20-5 is typically used for general purposes, hot or cold rolled sheet/plate and strip, while IS 6603 X01Ni25Cr20Mo5Cu is commonly used for general purposes, semi-finished products, bars, wire rods and bright bars.
EN 10088-2 X1NiCrMoCu25-20-5 is defined under European Standard (EN), originating from Europe, while IS 6603 X01Ni25Cr20Mo5Cu is defined under Bureau of Indian Standards (IS), originating from India.
As per chemical composition, EN 10088-2 X1NiCrMoCu25-20-5 vs IS 6603 X01Ni25Cr20Mo5Cu is a 93.9% match.
As per mechanical properties, the match is 66.7%.
Combined, this makes them a close alternative overall at 84.8%.
Frequently Compared With EN 10088-2 X1NiCrMoCu25-20-5:
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
EN 10088-2 X1NiCrMoCu25-20-5
IS 6603 X01Ni25Cr20Mo5Cu
Tensile Strength
530-730 MPa
530-730 MPa
Yield Strength
>=240 MPa
>=220 MPa
Elongation
>=35%
>=35%
Condition
Solution annealed (+AT), cold rolled strip, up to 8 mm thick; Yield Strength is Rp0.2 (transverse), Elongation is A80 for under 3 mm thick
Solution annealed, conditions 1C, 1E, 1D, 1X, 1G and 2D, thickness or diameter up to 160 mm; Yield Strength is Rp0.2, Elongation is A (longitudinal)
Typical Applications
EN 10088-2 X1NiCrMoCu25-20-5
General purposes, hot or cold rolled sheet/plate and strip
IS 6603 X01Ni25Cr20Mo5Cu
General purposes, semi-finished products, bars, wire rods and bright bars
Can EN 10088-2 X1NiCrMoCu25-20-5 Be Substituted With IS 6603 X01Ni25Cr20Mo5Cu?
EN 10088-2 X1NiCrMoCu25-20-5 and IS 6603 X01Ni25Cr20Mo5Cu are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
What is the difference between EN 10088-2 X1NiCrMoCu25-20-5 and IS 6603 X01Ni25Cr20Mo5Cu?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can EN 10088-2 X1NiCrMoCu25-20-5 be substituted with IS 6603 X01Ni25Cr20Mo5Cu?
EN 10088-2 X1NiCrMoCu25-20-5 and IS 6603 X01Ni25Cr20Mo5Cu are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.