EN 10088-2 X2CrNiMnMoN25-18-6-5 vs EN 10088-1 1.4401

Minimal Match — 32.3% match based on chemical composition and mechanical property overlap.

EN 10088-2 X2CrNiMnMoN25-18-6-5 (EN 10088-2:2014) and EN 10088-1 1.4401 (EN 10088-1:2014) are both steel grades. Both fall under the Stainless Steel category. EN 10088-2 X2CrNiMnMoN25-18-6-5 is typically used for general purposes, hot or cold rolled sheet/plate and strip, while EN 10088-1 1.4401 is commonly used for marine, chemical processing, pharmaceutical equipment. EN 10088-2 X2CrNiMnMoN25-18-6-5 is defined under European Standard (EN), originating from Europe, while EN 10088-1 1.4401 is defined under European Standard (EN), originating from Europe.

As per chemical composition, EN 10088-2 X2CrNiMnMoN25-18-6-5 vs EN 10088-1 1.4401 is a 48.5% match. As per mechanical properties, the match is 0%. Combined, this makes them a minimal match overall at 32.3%.

Frequently Compared With EN 10088-2 X2CrNiMnMoN25-18-6-5:
IS 1570 (Part 7) 12Cr12Ni2Mo ASTM A959 .- GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 GOST 5632 08X18H10 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4845 IS 1570 (Part 7) 12Cr13H IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH
Match Breakdown
CHEMISTRY MATCH
48.5%
MECHANICAL MATCH
0%
OVERALL
32.3%
Specifications
Property EN 10088-2 X2CrNiMnMoN25-18-6-5 EN 10088-1 1.4401
Standard EN 10088-2:2014 EN 10088-1:2014
Category Stainless Steel Stainless Steel
C (%) <=0.030 ≤0.07
Si (%) <=1.00 ≤1.00
Mn (%) 5.0-7.0 ≤2.00
P (%) <=0.030 Not specified
S (%) <=0.015 Not specified
Cr (%) 24.0-26.0 16.5–18.5
Mo (%) 4.0-5.0 2.0–2.5
Ni (%) 16.0-19.0 10.5–13.5
N (%) 0.30-0.60 Not specified
Nb (%) <=0.15 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property EN 10088-2 X2CrNiMnMoN25-18-6-5 EN 10088-1 1.4401
Tensile Strength 800-950 MPa ≥520 MPa
Yield Strength >=420 MPa ≥210 MPa
Elongation >=30% ≥40%
Condition Solution annealed (+AT), cold rolled strip, up to 6 mm thick; Yield Strength is Rp0.2 (transverse), Elongation is A80 for under 3 mm thick Not specified
Hardness Not specified ≤215 HB
Typical Applications
EN 10088-2 X2CrNiMnMoN25-18-6-5
General purposes, hot or cold rolled sheet/plate and strip
EN 10088-1 1.4401
Marine, chemical processing, pharmaceutical equipment
Key Differences
Can EN 10088-2 X2CrNiMnMoN25-18-6-5 Be Substituted With EN 10088-1 1.4401?
EN 10088-2 X2CrNiMnMoN25-18-6-5 and EN 10088-1 1.4401 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
EN 10088-2 X2CrNiMnMoN25-18-6-5
No active listings currently.
EN 10088-1 1.4401
Sheet → (4 listings)
Thickness: 6–6 mm (0.24–0.24 in)
Width: 1250–1250 mm (49.21–49.21 in)
Length: 2500–3400 mm (98.43–133.86 in)
On M-EX Right Now
EN 10088-2 X2CrNiMnMoN25-18-6-5
0 active listings and RFQs →
EN 10088-1 1.4401
4 active listings and RFQs →
Frequently Asked Questions
What is the difference between EN 10088-2 X2CrNiMnMoN25-18-6-5 and EN 10088-1 1.4401?
EN 10088-2 X2CrNiMnMoN25-18-6-5 specifies P, S, N, Nb which are not specified for EN 10088-1 1.4401.
Can EN 10088-2 X2CrNiMnMoN25-18-6-5 be substituted with EN 10088-1 1.4401?
EN 10088-2 X2CrNiMnMoN25-18-6-5 and EN 10088-1 1.4401 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.