EN 10088-2:2014 X2CrNiMnMoN25-18-6-5 Steel: Specifications & Listings

EN 10088-2:2014 X2CrNiMnMoN25-18-6-5: X2CrNiMnMoN25-18-6-5: austenitic corrosion resisting stainless steel, material number 1.4565. Specified in EN 10088-2:2014.

Category: Stainless Steel
Grade Details
GradeEN 10088-2:2014 X2CrNiMnMoN25-18-6-5
Standard EN 10088-2:2014
ApplicationsGeneral purposes, hot or cold rolled sheet/plate and strip
Equivalent / Similar Grades
Grade Standard Region Live on M-EX
ASTM A959 S34565 ASTM A959:2011 USA No activity yet
IS 6603 X02Cr25Ni18Mn6Mo4N IS 6603:2024 India No activity yet
EN 10088-1 X2CrNiMnMoN25-18-6-5 EN 10088-1:2014 Europe (CEN) No activity yet
EN 10088-3 X2CrNiMnMoN25-18-6-5 EN 10088-3:2014 Europe No activity yet
Grade ComparisonCompare With a Specific Grade →
Grade Standard Match
EN 10088-1 X2CrNiMnMoN25-18-6-5 EN 10088-1:2014 Strong Match
EN 10088-1 X2CrNiMnMoN25-18-6-5 EN 10088-1:2023 Strong Match
EN 10088-3 X2CrNiMnMoN25-18-6-5 EN 10088-3:2014 Strong Match
IS 6603 X02Cr25Ni18Mn6Mo4N IS 6603:2024 Strong Match
ASTM A959 S34565 ASTM A959:2011 Strong Match
EN 10088-1 X2CrNiMoN25-7-4 EN 10088-1:2014 Related Material
EN 10088-1 X2CrNiMoN25-7-4 EN 10088-1:2023 Related Material
ASTM A959 317LM ASTM A959:2011 Related Material
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Chemical Composition (%)
C Si Mn P S Cr Mo Ni N Nb
<=0.030 <=1.00 5.0-7.0 <=0.030 <=0.015 24.0-26.0 4.0-5.0 16.0-19.0 0.30-0.60 <=0.15
Mechanical Properties
Tensile Strength 800-950 MPa
Yield Strength >=420 MPa
Elongation >=30%
Condition Solution annealed (+AT), cold rolled strip, up to 6 mm thick; Yield Strength is Rp0.2 (transverse), Elongation is A80 for under 3 mm thick

More data from EN 10088-2:2014

From the standard
Mechanical properties by product form and thickness 3 product forms
Product formMax thickness (mm)Rp0.2 min (MPa)Rp1.0 min (MPa)Rm (MPa)A80 min, under 3 mm thick (%)A min, 3 mm and over (%)
Cold rolled strip6420460800 to 9503030
Hot rolled strip10420460800 to 9503030
Hot rolled plate40420460800 to 9503030
Solution annealed condition; proof strength and elongation are minimum transverse values.
Source: EN 10088-2:2014, Table 7
Impact energy KV2 (ISO-V) 3 rows
Product formMax thickness (mm)KV2 longitudinal, min (J)KV2 transverse, min (J)
Cold rolled strip612090
Hot rolled strip1012090
Hot rolled plate4012090
Applies to products more than 10 mm thick, ISO-V notch, room temperature.
Source: EN 10088-2:2014, Table 7
Proof strength at elevated temperature 10 temperatures
Temperature (deg C)Rp0.2 min (MPa)Rp1.0 min (MPa)
100350400
150310355
200270310
250255290
300240270
350225255
400210240
450210240
500210240
550200230
Minimum values, solution annealed (+AT).
Source: EN 10088-2:2014, Table 12
Hot forming and solution annealing guideline temperatures
Hot forming temperature
1200 to 950 deg C
Cooling after hot forming
air
Heat treatment symbol
+AT
Solution annealing temperature
1120 to 1170 deg C
Cooling after solution annealing
water, air
Informative guideline; cooling must be rapid enough to avoid intergranular corrosion.
Source: EN 10088-2:2014, Table A.1

Active EN 10088-2:2014 X2CrNiMnMoN25-18-6-5 Listings on M-EX (For Sale)

+ Create a Listing for this grade

No active EN 10088-2:2014 X2CrNiMnMoN25-18-6-5 listings at this time.

Register for Alerts

Buyer RFQs for EN 10088-2:2014 X2CrNiMnMoN25-18-6-5

+ Post an RFQ for this grade

No open buyer requirements for EN 10088-2:2014 X2CrNiMnMoN25-18-6-5 at this time.

Register for Alerts