EN 10088-2 X2CrNiMoCuWN25-7-4 vs EN 10088-1 X2CrNiMoCuN25-6-3

Strong Match — 87.2% match based on chemical composition and mechanical property overlap.

EN 10088-2 X2CrNiMoCuWN25-7-4 (EN 10088-2:2014) and EN 10088-1 X2CrNiMoCuN25-6-3 (EN 10088-1:2023) are both steel grades. Both fall under the Stainless Steel category. EN 10088-2 X2CrNiMoCuWN25-7-4 is defined under European Standard (EN), originating from Europe, while EN 10088-1 X2CrNiMoCuN25-6-3 is defined under European Standard (EN), originating from Europe.

As per chemical composition, EN 10088-2 X2CrNiMoCuWN25-7-4 vs EN 10088-1 X2CrNiMoCuN25-6-3 is a 87.2% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 87.2%.

Frequently Compared With EN 10088-2 X2CrNiMoCuWN25-7-4:
IS 1570 (Part 7) 12Cr12Ni2Mo GOST 5632 06Kh23N28 GOST 5632 08X18H10 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4401 EN 10088-1 1.4845 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH ASTM A959 .- GB/T 3280 06Cr19Ni10 IS 1570 (Part 7) 12Cr12MoVH
Match Breakdown
CHEMISTRY MATCH
87.2%
MECHANICAL MATCH
No shared data
OVERALL
87.2%
Specifications
Property EN 10088-2 X2CrNiMoCuWN25-7-4 EN 10088-1 X2CrNiMoCuN25-6-3
Standard EN 10088-2:2014 EN 10088-1:2023
Category Stainless Steel Stainless Steel
C (%) <=0.030 <=0.030
Si (%) <=1.00 <=0.70
Mn (%) <=1.00 <=2.00
P (%) <=0.035 <=0.035
S (%) <=0.015 <=0.015
Cr (%) 24.0-26.0 24.0-26.0
Mo (%) 3.0-4.0 3.00-4.0
Ni (%) 6.0-8.0 6.0-8.0
N (%) 0.20-0.30 0.20-0.30
Cu (%) 0.50-1.00 1.00-2.50
W (%) 0.50-1.00 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property EN 10088-2 X2CrNiMoCuWN25-7-4 EN 10088-1 X2CrNiMoCuN25-6-3
Tensile Strength 730-930 MPa Not specified
Yield Strength >=530 MPa Not specified
Elongation >=25% Not specified
Condition Solution annealed (+AT), hot rolled plate, up to 75 mm thick; Yield Strength is Rp0.2 (transverse), Elongation is A80 for under 3 mm thick Not specified
Typical Applications
EN 10088-2 X2CrNiMoCuWN25-7-4
General purposes, hot or cold rolled sheet/plate and strip
EN 10088-1 X2CrNiMoCuN25-6-3
Not documented
Key Differences
Can EN 10088-2 X2CrNiMoCuWN25-7-4 Be Substituted With EN 10088-1 X2CrNiMoCuN25-6-3?
EN 10088-2 X2CrNiMoCuWN25-7-4 and EN 10088-1 X2CrNiMoCuN25-6-3 overlap closely enough on chemistry and mechanical properties that EN 10088-1 X2CrNiMoCuN25-6-3 is often considered as a substitute for EN 10088-2 X2CrNiMoCuWN25-7-4 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
EN 10088-2 X2CrNiMoCuWN25-7-4
0 active listings and RFQs →
EN 10088-1 X2CrNiMoCuN25-6-3
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between EN 10088-2 X2CrNiMoCuWN25-7-4 and EN 10088-1 X2CrNiMoCuN25-6-3?
EN 10088-2 X2CrNiMoCuWN25-7-4 specifies W which is not specified for EN 10088-1 X2CrNiMoCuN25-6-3.
Can EN 10088-2 X2CrNiMoCuWN25-7-4 be substituted with EN 10088-1 X2CrNiMoCuN25-6-3?
EN 10088-2 X2CrNiMoCuWN25-7-4 and EN 10088-1 X2CrNiMoCuN25-6-3 overlap closely enough on chemistry and mechanical properties that EN 10088-1 X2CrNiMoCuN25-6-3 is often considered as a substitute for EN 10088-2 X2CrNiMoCuWN25-7-4 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.