EN 10088-2 X2CrNiMoCuWN25-7-4 vs IS 6603 X02Cr25Ni7Mo4CuWN
Strong Match — 88.9% match
based on chemical composition and mechanical property overlap.
EN 10088-2 X2CrNiMoCuWN25-7-4 (EN 10088-2:2014) and IS 6603 X02Cr25Ni7Mo4CuWN (IS 6603:2024) are both steel grades.
Both fall under the Stainless Steel category.
EN 10088-2 X2CrNiMoCuWN25-7-4 is typically used for general purposes, hot or cold rolled sheet/plate and strip, while IS 6603 X02Cr25Ni7Mo4CuWN is commonly used for general purposes, semi-finished products, bars, wire rods and bright bars.
EN 10088-2 X2CrNiMoCuWN25-7-4 is defined under European Standard (EN), originating from Europe, while IS 6603 X02Cr25Ni7Mo4CuWN is defined under Bureau of Indian Standards (IS), originating from India.
As per chemical composition, EN 10088-2 X2CrNiMoCuWN25-7-4 vs IS 6603 X02Cr25Ni7Mo4CuWN is a 100% match.
As per mechanical properties, the match is 66.7%.
Combined, this makes them a strong match overall at 88.9%.
Frequently Compared With EN 10088-2 X2CrNiMoCuWN25-7-4:
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
EN 10088-2 X2CrNiMoCuWN25-7-4
IS 6603 X02Cr25Ni7Mo4CuWN
Tensile Strength
730-930 MPa
>=730 MPa
Yield Strength
>=530 MPa
>=530 MPa
Elongation
>=25%
>=25%
Condition
Solution annealed (+AT), hot rolled plate, up to 75 mm thick; Yield Strength is Rp0.2 (transverse), Elongation is A80 for under 3 mm thick
Solution annealed, conditions 1C, 1E, 1D, 1X, 1G and 2D, thickness or diameter up to 160 mm; Tensile Strength is a minimum as printed, hardness for guidance only
Hardness
Not specified
<=290 HB
Typical Applications
EN 10088-2 X2CrNiMoCuWN25-7-4
General purposes, hot or cold rolled sheet/plate and strip
IS 6603 X02Cr25Ni7Mo4CuWN
General purposes, semi-finished products, bars, wire rods and bright bars
Can EN 10088-2 X2CrNiMoCuWN25-7-4 Be Substituted With IS 6603 X02Cr25Ni7Mo4CuWN?
EN 10088-2 X2CrNiMoCuWN25-7-4 and IS 6603 X02Cr25Ni7Mo4CuWN overlap closely enough on chemistry and mechanical properties that IS 6603 X02Cr25Ni7Mo4CuWN is often considered as a substitute for EN 10088-2 X2CrNiMoCuWN25-7-4 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
What is the difference between EN 10088-2 X2CrNiMoCuWN25-7-4 and IS 6603 X02Cr25Ni7Mo4CuWN?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can EN 10088-2 X2CrNiMoCuWN25-7-4 be substituted with IS 6603 X02Cr25Ni7Mo4CuWN?
EN 10088-2 X2CrNiMoCuWN25-7-4 and IS 6603 X02Cr25Ni7Mo4CuWN overlap closely enough on chemistry and mechanical properties that IS 6603 X02Cr25Ni7Mo4CuWN is often considered as a substitute for EN 10088-2 X2CrNiMoCuWN25-7-4 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.