EN 10088-2 X2CrNiMoN25-7-4 vs EN 10088-1 X2CrNiMoCuWN25-7-4

Close Alternative — 82.8% match based on chemical composition and mechanical property overlap.

EN 10088-2 X2CrNiMoN25-7-4 (EN 10088-2:2014) and EN 10088-1 X2CrNiMoCuWN25-7-4 (EN 10088-1:2014) are both steel grades. Both fall under the Stainless Steel category. EN 10088-2 X2CrNiMoN25-7-4 is defined under European Standard (EN), originating from Europe, while EN 10088-1 X2CrNiMoCuWN25-7-4 is defined under European Standard (EN), originating from Europe.

As per chemical composition, EN 10088-2 X2CrNiMoN25-7-4 vs EN 10088-1 X2CrNiMoCuWN25-7-4 is a 82.8% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a close alternative overall at 82.8%.

Frequently Compared With EN 10088-2 X2CrNiMoN25-7-4:
ASTM A959 2507 GB/T 3280 06Cr19Ni10 GOST 5632 08X18H10 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4401 EN 10088-1 1.4845 IS 1570 (Part 7) 11Cr17Ni13W3TiH ASTM A959 .- GOST 5632 06Kh23N28 IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH
Match Breakdown
CHEMISTRY MATCH
82.8%
MECHANICAL MATCH
No shared data
OVERALL
82.8%
Specifications
Property EN 10088-2 X2CrNiMoN25-7-4 EN 10088-1 X2CrNiMoCuWN25-7-4
Standard EN 10088-2:2014 EN 10088-1:2014
Category Stainless Steel Stainless Steel
C (%) <=0.030 <=0.030
Si (%) <=1.00 <=1.00
Mn (%) <=2.00 <=1.00
P (%) <=0.035 <=0.035
S (%) <=0.015 <=0.015
Cr (%) 24.0-26.0 24.0-26.0
Mo (%) 3.0-4.5 3.0-4.0
Ni (%) 6.0-8.0 6.0-8.0
N (%) 0.24-0.35 0.20-0.30
Cu (%) Not specified 0.50-1.00
W (%) Not specified 0.50-1.00
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property EN 10088-2 X2CrNiMoN25-7-4 EN 10088-1 X2CrNiMoCuWN25-7-4
Tensile Strength 750-1000 MPa Not specified
Yield Strength >=550 MPa Not specified
Elongation >=20% Not specified
Condition Solution annealed (+AT), cold rolled strip, up to 8 mm thick; Yield Strength is Rp0.2 (transverse), Elongation is A80 for under 3 mm thick Not specified
Typical Applications
EN 10088-2 X2CrNiMoN25-7-4
General purposes, hot or cold rolled sheet/plate and strip
EN 10088-1 X2CrNiMoCuWN25-7-4
Not documented
Key Differences
Can EN 10088-2 X2CrNiMoN25-7-4 Be Substituted With EN 10088-1 X2CrNiMoCuWN25-7-4?
EN 10088-2 X2CrNiMoN25-7-4 and EN 10088-1 X2CrNiMoCuWN25-7-4 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
On M-EX Right Now
EN 10088-2 X2CrNiMoN25-7-4
0 active listings and RFQs →
EN 10088-1 X2CrNiMoCuWN25-7-4
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between EN 10088-2 X2CrNiMoN25-7-4 and EN 10088-1 X2CrNiMoCuWN25-7-4?
EN 10088-1 X2CrNiMoCuWN25-7-4 specifies Cu, W which are not specified for EN 10088-2 X2CrNiMoN25-7-4.
Can EN 10088-2 X2CrNiMoN25-7-4 be substituted with EN 10088-1 X2CrNiMoCuWN25-7-4?
EN 10088-2 X2CrNiMoN25-7-4 and EN 10088-1 X2CrNiMoCuWN25-7-4 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.