EN 10088-2 X2CrNiMoN29-7-2 vs ASTM A959 2507

Related Material — 67.5% match based on chemical composition and mechanical property overlap.

EN 10088-2 X2CrNiMoN29-7-2 (EN 10088-2:2014) and ASTM A959 2507 (ASTM A959:2011) are both steel grades. Both fall under the Stainless Steel category. EN 10088-2 X2CrNiMoN29-7-2 is typically used for general purposes, hot or cold rolled sheet/plate and strip, while ASTM A959 2507 is commonly used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1). EN 10088-2 X2CrNiMoN29-7-2 is defined under European Standard (EN), originating from Europe, while ASTM A959 2507 is defined under ASTM International, originating from United States.

As per chemical composition, EN 10088-2 X2CrNiMoN29-7-2 vs ASTM A959 2507 is a 67.5% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a related material overall at 67.5%.

Frequently Compared With EN 10088-2 X2CrNiMoN29-7-2:
IS 1570 (Part 7) 12Cr12MoVH GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 GOST 5632 08X18H10 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4401 EN 10088-1 1.4845 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH ASTM A959 .- IS 1570 (Part 7) 12Cr12Ni2Mo
Match Breakdown
CHEMISTRY MATCH
67.5%
MECHANICAL MATCH
No shared data
OVERALL
67.5%
Specifications
Property EN 10088-2 X2CrNiMoN29-7-2 ASTM A959 2507
Standard EN 10088-2:2014 ASTM A959:2011
Category Stainless Steel Stainless Steel
C (%) <=0.030 <=0.030
Si (%) <=0.50 <=0.80
Mn (%) 0.80-1.50 <=1.20
P (%) <=0.030 <=0.035
S (%) <=0.015 <=0.020
Cr (%) 28.0-30.0 24.0-26.0
Mo (%) 1.50-2.60 3.0-5.0
Ni (%) 5.8-7.5 6.0-8.0
N (%) 0.30-0.40 0.24-0.32
Cu (%) <=0.80 <=0.50
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property EN 10088-2 X2CrNiMoN29-7-2 ASTM A959 2507
Tensile Strength 800-1050 MPa Not specified
Yield Strength >=650 MPa Not specified
Elongation >=20% Not specified
Condition Solution annealed (+AT), cold rolled strip, up to 8 mm thick; Yield Strength is Rp0.2 (transverse), Elongation is A80 for under 3 mm thick Not specified
Typical Applications
EN 10088-2 X2CrNiMoN29-7-2
General purposes, hot or cold rolled sheet/plate and strip
ASTM A959 2507
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
Can EN 10088-2 X2CrNiMoN29-7-2 Be Substituted With ASTM A959 2507?
EN 10088-2 X2CrNiMoN29-7-2 and ASTM A959 2507 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
EN 10088-2 X2CrNiMoN29-7-2
0 active listings and RFQs →
ASTM A959 2507
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between EN 10088-2 X2CrNiMoN29-7-2 and ASTM A959 2507?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can EN 10088-2 X2CrNiMoN29-7-2 be substituted with ASTM A959 2507?
EN 10088-2 X2CrNiMoN29-7-2 and ASTM A959 2507 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.