EN 10088-2 X2CrNiMoSi18-5-3 vs EN 10088-1 X2CrNiMoN17-13-3

Related Material — 69.9% match based on chemical composition and mechanical property overlap.

EN 10088-2 X2CrNiMoSi18-5-3 (EN 10088-2:2014) and EN 10088-1 X2CrNiMoN17-13-3 (EN 10088-1:2014) are both steel grades. Both fall under the Stainless Steel category. EN 10088-2 X2CrNiMoSi18-5-3 is defined under European Standard (EN), originating from Europe, while EN 10088-1 X2CrNiMoN17-13-3 is defined under European Standard (EN), originating from Europe.

As per chemical composition, EN 10088-2 X2CrNiMoSi18-5-3 vs EN 10088-1 X2CrNiMoN17-13-3 is a 69.9% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a related material overall at 69.9%.

Frequently Compared With EN 10088-2 X2CrNiMoSi18-5-3:
GOST 5632 06Kh23N28 GOST 5632 08X18H10 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4401 EN 10088-1 1.4845 IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12Ni2Mo ASTM A959 .- GB/T 3280 06Cr19Ni10 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoVH
Match Breakdown
CHEMISTRY MATCH
69.9%
MECHANICAL MATCH
No shared data
OVERALL
69.9%
Specifications
Property EN 10088-2 X2CrNiMoSi18-5-3 EN 10088-1 X2CrNiMoN17-13-3
Standard EN 10088-2:2014 EN 10088-1:2014
Category Stainless Steel Stainless Steel
C (%) <=0.030 <=0.030
Si (%) 1.40-2.00 <=1.00
Mn (%) 1.20-2.00 <=2.00
P (%) <=0.035 <=0.045
S (%) <=0.015 <=0.015
Cr (%) 18.0-19.0 16.5-18.5
Mo (%) 2.50-3.0 2.50-3.00
Ni (%) 4.5-5.2 11.0-14.0
N (%) 0.05-0.10 0.12-0.22
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property EN 10088-2 X2CrNiMoSi18-5-3 EN 10088-1 X2CrNiMoN17-13-3
Tensile Strength 700-900 MPa Not specified
Yield Strength >=450 MPa Not specified
Elongation >=25% Not specified
Condition Solution annealed (+AT), cold rolled strip, up to 8 mm thick; Yield Strength is Rp0.2 (transverse), Elongation is A80 for under 3 mm thick Not specified
Typical Applications
EN 10088-2 X2CrNiMoSi18-5-3
General purposes, hot or cold rolled sheet/plate and strip
EN 10088-1 X2CrNiMoN17-13-3
Not documented
Can EN 10088-2 X2CrNiMoSi18-5-3 Be Substituted With EN 10088-1 X2CrNiMoN17-13-3?
EN 10088-2 X2CrNiMoSi18-5-3 and EN 10088-1 X2CrNiMoN17-13-3 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
EN 10088-2 X2CrNiMoSi18-5-3
0 active listings and RFQs →
EN 10088-1 X2CrNiMoN17-13-3
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between EN 10088-2 X2CrNiMoSi18-5-3 and EN 10088-1 X2CrNiMoN17-13-3?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can EN 10088-2 X2CrNiMoSi18-5-3 be substituted with EN 10088-1 X2CrNiMoN17-13-3?
EN 10088-2 X2CrNiMoSi18-5-3 and EN 10088-1 X2CrNiMoN17-13-3 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.