EN 10088-2 X2CrTi17 vs GB/T 3280 06Cr19Ni10

Minimal Match — 35% match based on chemical composition and mechanical property overlap.

EN 10088-2 X2CrTi17 (EN 10088-2:2014) and GB/T 3280 06Cr19Ni10 (GB/T 3280-2015) are both steel grades. Both fall under the Stainless Steel category. EN 10088-2 X2CrTi17 is typically used for general purposes, hot or cold rolled sheet/plate and strip, while GB/T 3280 06Cr19Ni10 is commonly used for used for kitchen equipment, food processing machinery, chemical tanks, piping, architectural panels, and fasteners.. EN 10088-2 X2CrTi17 is defined under European Standard (EN), originating from Europe, while GB/T 3280 06Cr19Ni10 is defined under Guobiao Standards (GB/T), originating from China.

As per chemical composition, EN 10088-2 X2CrTi17 vs GB/T 3280 06Cr19Ni10 is a 59.9% match. As per mechanical properties, the match is 1%. Combined, this makes them a minimal match overall at 35%.

Frequently Compared With EN 10088-2 X2CrTi17:
ASTM A959 .- EN 10088-1 1.4401 IS 1570 (Part 7) 12Cr13H GOST 5632 06Kh23N28 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4845 GOST 5632 08X18H10 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr12Ni2Mo
Match Breakdown
CHEMISTRY MATCH
59.9%
MECHANICAL MATCH
1%
OVERALL
35%
Specifications
Property EN 10088-2 X2CrTi17 GB/T 3280 06Cr19Ni10
Standard EN 10088-2:2014 GB/T 3280-2015
Category Stainless Steel Stainless Steel
C (%) <=0.025 0.08 max
Si (%) <=0.50 1.00 max
Mn (%) <=0.50 2.00 max
P (%) <=0.040 0.045 max
S (%) <=0.015 0.030 max
Cr (%) 16.0-18.0 18.00-20.00
N (%) <=0.015 Not specified
Ti (%) <=0.80 Not specified
Ni (%) Not specified 8.00-11.00
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property EN 10088-2 X2CrTi17 GB/T 3280 06Cr19Ni10
Tensile Strength 380-530 MPa 520-720 MPa
Condition Annealed (+A), cold rolled strip, up to 8 mm thick; Elongation is A80 (under 3 mm) or A (3 mm and over), longitudinal and transverse Not specified
Yield Strength >=180 MPa 205-310 MPa
Elongation >=24% 40-60%
Hardness Not specified 187 HB max
Typical Applications
EN 10088-2 X2CrTi17
General purposes, hot or cold rolled sheet/plate and strip
GB/T 3280 06Cr19Ni10
Used for kitchen equipment, food processing machinery, chemical tanks, piping, architectural panels, and fasteners.
Key Differences
Can EN 10088-2 X2CrTi17 Be Substituted With GB/T 3280 06Cr19Ni10?
EN 10088-2 X2CrTi17 and GB/T 3280 06Cr19Ni10 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
EN 10088-2 X2CrTi17
No active listings currently.
GB/T 3280 06Cr19Ni10
Sheet → (2 listings)
Thickness: 6–6 mm (0.24–0.24 in)
Width: 1250–1250 mm (49.21–49.21 in)
Length: 2900–3300 mm (114.17–129.92 in)
On M-EX Right Now
EN 10088-2 X2CrTi17
0 active listings and RFQs →
GB/T 3280 06Cr19Ni10
2 active listings and RFQs →
Frequently Asked Questions
What is the difference between EN 10088-2 X2CrTi17 and GB/T 3280 06Cr19Ni10?
EN 10088-2 X2CrTi17 specifies N, Ti which are not specified for GB/T 3280 06Cr19Ni10. GB/T 3280 06Cr19Ni10 specifies Ni which is not specified for EN 10088-2 X2CrTi17.
Can EN 10088-2 X2CrTi17 be substituted with GB/T 3280 06Cr19Ni10?
EN 10088-2 X2CrTi17 and GB/T 3280 06Cr19Ni10 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.