Minimal Match — 35% match
based on chemical composition and mechanical property overlap.
EN 10088-2 X2CrTi17 (EN 10088-2:2014) and IS 1570 (Part 7) 12Cr13H (IS 1570 (Part 7):1992) are both steel grades.
Both fall under the Stainless Steel category.
EN 10088-2 X2CrTi17 is typically used for general purposes, hot or cold rolled sheet/plate and strip, while IS 1570 (Part 7) 12Cr13H is commonly used for boilers, pressure vessels, steam turbines, steam and water piping and other power plant equipment working at elevated temperature.
EN 10088-2 X2CrTi17 is defined under European Standard (EN), originating from Europe, while IS 1570 (Part 7) 12Cr13H is defined under Bureau of Indian Standards (IS), originating from India.
As per chemical composition, EN 10088-2 X2CrTi17 vs IS 1570 (Part 7) 12Cr13H is a 59.4% match.
As per mechanical properties, the match is 6.9%.
Combined, this makes them a minimal match overall at 35%.
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
EN 10088-2 X2CrTi17
IS 1570 (Part 7) 12Cr13H
Tensile Strength
380-530 MPa
470-670 MPa
Condition
Annealed (+A), cold rolled strip, up to 8 mm thick; Elongation is A80 (under 3 mm) or A (3 mm and over), longitudinal and transverse
Bars, forgings, plates, A, thickness up to 160 (first row of Table 3)
Yield Strength
>=180 MPa
>=265 MPa (0.2 % proof stress)
Elongation
>=24%
>=20%
Typical Applications
EN 10088-2 X2CrTi17
General purposes, hot or cold rolled sheet/plate and strip
IS 1570 (Part 7) 12Cr13H
Boilers, pressure vessels, steam turbines, steam and water piping and other power plant equipment working at elevated temperature
Key Differences
EN 10088-2 X2CrTi17 specifies N, Ti which are not specified for IS 1570 (Part 7) 12Cr13H.
IS 1570 (Part 7) 12Cr13H specifies Ni which is not specified for EN 10088-2 X2CrTi17.
Can EN 10088-2 X2CrTi17 Be Substituted With IS 1570 (Part 7) 12Cr13H?
EN 10088-2 X2CrTi17 and IS 1570 (Part 7) 12Cr13H share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
What is the difference between EN 10088-2 X2CrTi17 and IS 1570 (Part 7) 12Cr13H?
EN 10088-2 X2CrTi17 specifies N, Ti which are not specified for IS 1570 (Part 7) 12Cr13H. IS 1570 (Part 7) 12Cr13H specifies Ni which is not specified for EN 10088-2 X2CrTi17.
Can EN 10088-2 X2CrTi17 be substituted with IS 1570 (Part 7) 12Cr13H?
EN 10088-2 X2CrTi17 and IS 1570 (Part 7) 12Cr13H share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.