Minimal Match — 35% match
based on chemical composition and mechanical property overlap.
EN 10088-2 X3CrNiMo17-13-3 (EN 10088-2:2014) and GOST 5632 08X18H10 (GOST 5632-2014) are both steel grades.
Both fall under the Stainless Steel category.
EN 10088-2 X3CrNiMo17-13-3 is typically used for general purposes, hot or cold rolled sheet/plate and strip, while GOST 5632 08X18H10 is commonly used for chemical equipment, food processing, general corrosion resistant applications.
EN 10088-2 X3CrNiMo17-13-3 is defined under European Standard (EN) (Europe).
As per chemical composition, EN 10088-2 X3CrNiMo17-13-3 vs GOST 5632 08X18H10 is a 65.3% match.
As per mechanical properties, the match is 33.3%.
Combined, this makes them a minimal match overall at 35%.
Frequently Compared With EN 10088-2 X3CrNiMo17-13-3:
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
EN 10088-2 X3CrNiMo17-13-3
GOST 5632 08X18H10
Tensile Strength
550-700 MPa
≥520 MPa
Yield Strength
>=240 MPa
≥205 MPa
Elongation
>=40%
≥40%
Condition
Solution annealed (+AT), cold rolled strip, up to 8 mm thick; Yield Strength is Rp0.2 (transverse), Elongation is A80 for under 3 mm thick
Not specified
Typical Applications
EN 10088-2 X3CrNiMo17-13-3
General purposes, hot or cold rolled sheet/plate and strip
GOST 5632 08X18H10
Chemical equipment, food processing, general corrosion resistant applications
Key Differences
EN 10088-2 X3CrNiMo17-13-3 specifies Mo, N which are not specified for GOST 5632 08X18H10.
Can EN 10088-2 X3CrNiMo17-13-3 Be Substituted With GOST 5632 08X18H10?
EN 10088-2 X3CrNiMo17-13-3 and GOST 5632 08X18H10 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
What is the difference between EN 10088-2 X3CrNiMo17-13-3 and GOST 5632 08X18H10?
EN 10088-2 X3CrNiMo17-13-3 specifies Mo, N which are not specified for GOST 5632 08X18H10.
Can EN 10088-2 X3CrNiMo17-13-3 be substituted with GOST 5632 08X18H10?
EN 10088-2 X3CrNiMo17-13-3 and GOST 5632 08X18H10 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.