EN 10088-2 X3CrNiMo17-13-3 vs IS 1570 (Part 7) 12Cr12MoVH

Minimal Match — 33.6% match based on chemical composition and mechanical property overlap.

EN 10088-2 X3CrNiMo17-13-3 (EN 10088-2:2014) and IS 1570 (Part 7) 12Cr12MoVH (IS 1570 (Part 7):1992) are both steel grades. Both fall under the Stainless Steel category. EN 10088-2 X3CrNiMo17-13-3 is typically used for general purposes, hot or cold rolled sheet/plate and strip, while IS 1570 (Part 7) 12Cr12MoVH is commonly used for boilers, pressure vessels, steam turbines, steam and water piping and other power plant equipment working at elevated temperature. EN 10088-2 X3CrNiMo17-13-3 is defined under European Standard (EN), originating from Europe, while IS 1570 (Part 7) 12Cr12MoVH is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, EN 10088-2 X3CrNiMo17-13-3 vs IS 1570 (Part 7) 12Cr12MoVH is a 50.3% match. As per mechanical properties, the match is 0%. Combined, this makes them a minimal match overall at 33.6%.

Frequently Compared With EN 10088-2 X3CrNiMo17-13-3:
EN 10088-1 1.4401 EN 10088-1 1.4845 GOST 5632 08X18H10 EN 10088-1 1.4006 EN 10088-1 1.4301 IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12Ni2Mo ASTM A959 .- GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr13H
Match Breakdown
CHEMISTRY MATCH
50.3%
MECHANICAL MATCH
0%
OVERALL
33.6%
Specifications
Property EN 10088-2 X3CrNiMo17-13-3 IS 1570 (Part 7) 12Cr12MoVH
Standard EN 10088-2:2014 IS 1570 (Part 7):1992
Category Stainless Steel Stainless Steel
C (%) <=0.05 0.08-0.16
Si (%) <=1.00 <=0.60
Mn (%) <=2.00 0.40-1.00
P (%) <=0.045 <=0.040
S (%) <=0.015 <=0.035
Cr (%) 16.5-18.5 11.5-13.00
Mo (%) 2.50-3.00 0.40-0.80
Ni (%) 10.5-13.0 <=1.0
N (%) <=0.10 Not specified
V (%) Not specified 0.10-0.30
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property EN 10088-2 X3CrNiMo17-13-3 IS 1570 (Part 7) 12Cr12MoVH
Tensile Strength 550-700 MPa 770-930 MPa
Yield Strength >=240 MPa >=585 MPa (0.2 % proof stress)
Elongation >=40% >=15%
Condition Solution annealed (+AT), cold rolled strip, up to 8 mm thick; Yield Strength is Rp0.2 (transverse), Elongation is A80 for under 3 mm thick Bars, forgings, Q+T, thickness up to 150 (first row of Table 3)
Typical Applications
EN 10088-2 X3CrNiMo17-13-3
General purposes, hot or cold rolled sheet/plate and strip
IS 1570 (Part 7) 12Cr12MoVH
Boilers, pressure vessels, steam turbines, steam and water piping and other power plant equipment working at elevated temperature
Key Differences
Can EN 10088-2 X3CrNiMo17-13-3 Be Substituted With IS 1570 (Part 7) 12Cr12MoVH?
EN 10088-2 X3CrNiMo17-13-3 and IS 1570 (Part 7) 12Cr12MoVH share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
EN 10088-2 X3CrNiMo17-13-3
0 active listings and RFQs →
IS 1570 (Part 7) 12Cr12MoVH
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between EN 10088-2 X3CrNiMo17-13-3 and IS 1570 (Part 7) 12Cr12MoVH?
EN 10088-2 X3CrNiMo17-13-3 specifies N which is not specified for IS 1570 (Part 7) 12Cr12MoVH. IS 1570 (Part 7) 12Cr12MoVH specifies V which is not specified for EN 10088-2 X3CrNiMo17-13-3.
Can EN 10088-2 X3CrNiMo17-13-3 be substituted with IS 1570 (Part 7) 12Cr12MoVH?
EN 10088-2 X3CrNiMo17-13-3 and IS 1570 (Part 7) 12Cr12MoVH share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.