EN 10088-2 X50CrMoV15 vs GOST 5632 06Kh23N28

Minimal Match — 32% match based on chemical composition and mechanical property overlap.

EN 10088-2 X50CrMoV15 (EN 10088-2:2014) and GOST 5632 06Kh23N28 (GOST 5632-2014) are both steel grades. Both fall under the Stainless Steel category. EN 10088-2 X50CrMoV15 is typically used for general purposes, hot or cold rolled sheet/plate and strip, while GOST 5632 06Kh23N28 is commonly used for furnace components, heat exchangers, high temperature applications. EN 10088-2 X50CrMoV15 is defined under European Standard (EN) (Europe).

As per chemical composition, EN 10088-2 X50CrMoV15 vs GOST 5632 06Kh23N28 is a 48.1% match. As per mechanical properties, the match is 0%. Combined, this makes them a minimal match overall at 32%.

Frequently Compared With EN 10088-2 X50CrMoV15:
ASTM A959 .- GB/T 3280 06Cr19Ni10 GOST 5632 08X18H10 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4401 EN 10088-1 1.4845 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr12Ni2Mo IS 1570 (Part 7) 12Cr13H
Match Breakdown
CHEMISTRY MATCH
48.1%
MECHANICAL MATCH
0%
OVERALL
32%
Specifications
Property EN 10088-2 X50CrMoV15 GOST 5632 06Kh23N28
Standard EN 10088-2:2014 GOST 5632-2014
Category Stainless Steel Stainless Steel
C (%) 0.45-0.55 ≤0.06
Si (%) <=1.00 ≤0.80
Mn (%) <=1.00 ≤2.00
P (%) <=0.040 Not specified
S (%) <=0.015 Not specified
Cr (%) 14.0-15.0 22.0–25.0
Mo (%) 0.50-0.80 Not specified
V (%) 0.10-0.20 Not specified
Ni (%) Not specified 26.0–29.0
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property EN 10088-2 X50CrMoV15 GOST 5632 06Kh23N28
Tensile Strength <=850 MPa ≥510 MPa
Elongation >=12% ≥35%
Hardness <=280 HB Not specified
Condition Annealed (+A), cold rolled strip, up to 8 mm thick Not specified
Yield Strength Not specified ≥196 MPa
Max Service Temp Not specified 1050°C
Typical Applications
EN 10088-2 X50CrMoV15
General purposes, hot or cold rolled sheet/plate and strip
GOST 5632 06Kh23N28
Furnace components, heat exchangers, high temperature applications
Key Differences
Can EN 10088-2 X50CrMoV15 Be Substituted With GOST 5632 06Kh23N28?
EN 10088-2 X50CrMoV15 and GOST 5632 06Kh23N28 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
EN 10088-2 X50CrMoV15
No active listings currently.
GOST 5632 06Kh23N28
Sheet → (2 listings)
Thickness: 6–6 mm (0.24–0.24 in)
Width: 1250–1250 mm (49.21–49.21 in)
Length: 3100–3400 mm (122.05–133.86 in)
On M-EX Right Now
EN 10088-2 X50CrMoV15
0 active listings and RFQs →
GOST 5632 06Kh23N28
2 active listings and RFQs →
Frequently Asked Questions
What is the difference between EN 10088-2 X50CrMoV15 and GOST 5632 06Kh23N28?
EN 10088-2 X50CrMoV15 specifies P, S, Mo, V which are not specified for GOST 5632 06Kh23N28. GOST 5632 06Kh23N28 specifies Ni which is not specified for EN 10088-2 X50CrMoV15.
Can EN 10088-2 X50CrMoV15 be substituted with GOST 5632 06Kh23N28?
EN 10088-2 X50CrMoV15 and GOST 5632 06Kh23N28 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.