EN 10088-2:2014 X5CrNiMo17-12-2 Steel: Specifications & Listings
EN 10088-2:2014 X5CrNiMo17-12-2: X5CrNiMo17-12-2: austenitic corrosion resisting stainless steel, material number 1.4401. Specified in EN 10088-2:2014.
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Chemical Composition (%)
C
Si
Mn
P
S
Cr
Mo
Ni
N
<=0.07
<=1.00
<=2.00
<=0.045
<=0.015
16.5-18.5
2.00-2.50
10.0-13.0
<=0.10
Mechanical Properties
Tensile Strength
530-680 MPa
Yield Strength
>=240 MPa
Elongation
>=40%
Condition
Solution annealed (+AT), cold rolled strip, up to 8 mm thick; Yield Strength is Rp0.2 (transverse), Elongation is A80 for under 3 mm thick
More data from EN 10088-2:2014
From the standard
Mechanical properties by product form and thickness3 product forms
Product form
Max thickness (mm)
Rp0.2 min (MPa)
Rp1.0 min (MPa)
Rm (MPa)
A80 min, under 3 mm thick (%)
A min, 3 mm and over (%)
Cold rolled strip
8
240
270
530 to 680
40
40
Hot rolled strip
13.5
220
260
530 to 680
40
40
Hot rolled plate
75
220
260
520 to 670
45
45
Solution annealed condition; proof strength and elongation are minimum transverse values.
Source: EN 10088-2:2014, Table 7
Impact energy KV2 (ISO-V)2 rows
Product form
Max thickness (mm)
KV2 longitudinal, min (J)
KV2 transverse, min (J)
Hot rolled strip
13.5
100
60
Hot rolled plate
75
100
60
Applies to products more than 10 mm thick, ISO-V notch, room temperature.
Source: EN 10088-2:2014, Table 7
Proof strength at elevated temperature10 temperatures
Temperature (deg C)
Rp0.2 min (MPa)
Rp1.0 min (MPa)
100
177
211
150
162
191
200
147
177
250
137
167
300
127
156
350
120
150
400
115
144
450
112
141
500
110
139
550
108
137
Minimum values, solution annealed (+AT).
Source: EN 10088-2:2014, Table 12
Hot forming and solution annealingguideline temperatures
Hot forming temperature
1150 to 850 deg C
Cooling after hot forming
air
Heat treatment symbol
+AT
Solution annealing temperature
1030 to 1110 deg C
Cooling after solution annealing
water, air
Informative guideline; cooling must be rapid enough to avoid intergranular corrosion.
Source: EN 10088-2:2014, Table A.1
Cold worked condition levels (process route 2H)cold worked levels
Available tensile strength levels
+C700 (700 to 850 MPa); +C850 (850 to 1000 MPa)
Available 0.2% proof strength levels
+CP350 (350 to 500 MPa); +CP500 (500 to 700 MPa)
Only one parameter (tensile strength or proof strength) can be specified in the order.
Source: EN 10088-2:2014, Table 19 and 20