EN 10088-2 X6CrMnNiCuN18-12-4-2 vs EN 10088-1 X6CrNiCuS18-9-2

Related Material — 69.9% match based on chemical composition and mechanical property overlap.

EN 10088-2 X6CrMnNiCuN18-12-4-2 (EN 10088-2:2014) and EN 10088-1 X6CrNiCuS18-9-2 (EN 10088-1:2023) are both steel grades. Both fall under the Stainless Steel category. EN 10088-2 X6CrMnNiCuN18-12-4-2 is defined under European Standard (EN), originating from Europe, while EN 10088-1 X6CrNiCuS18-9-2 is defined under European Standard (EN), originating from Europe.

As per chemical composition, EN 10088-2 X6CrMnNiCuN18-12-4-2 vs EN 10088-1 X6CrNiCuS18-9-2 is a 70.5% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a related material overall at 69.9%.

Frequently Compared With EN 10088-2 X6CrMnNiCuN18-12-4-2:
GOST 5632 06Kh23N28 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4401 EN 10088-1 1.4845 IS 1570 (Part 7) 11Cr17Ni13W3TiH ASTM A959 .- GB/T 3280 06Cr19Ni10 GOST 5632 08X18H10 IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr12Ni2Mo
Match Breakdown
CHEMISTRY MATCH
70.5%
MECHANICAL MATCH
No shared data
OVERALL
69.9%
Specifications
Property EN 10088-2 X6CrMnNiCuN18-12-4-2 EN 10088-1 X6CrNiCuS18-9-2
Standard EN 10088-2:2014 EN 10088-1:2023
Category Stainless Steel Stainless Steel
C (%) 0.02-0.10 <=0.08
Si (%) <=1.00 <=1.00
Mn (%) 10.5-12.5 <=2.00
P (%) <=0.050 <=0.045
S (%) <=0.015 0.15-0.35
Cr (%) 17.0-19.0 17.0-19.0
Mo (%) <=0.50 <=0.60
Ni (%) 3.5-4.5 8.0-10.0
N (%) 0.20-0.30 <=0.10
Cu (%) 1.50-3.00 1.40-1.80
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property EN 10088-2 X6CrMnNiCuN18-12-4-2 EN 10088-1 X6CrNiCuS18-9-2
Tensile Strength 650-850 MPa Not specified
Yield Strength >=380 MPa Not specified
Elongation >=30% Not specified
Condition Solution annealed (+AT), cold rolled strip, up to 8 mm thick; Yield Strength is Rp0.2 (transverse), Elongation is A80 for under 3 mm thick Not specified
Typical Applications
EN 10088-2 X6CrMnNiCuN18-12-4-2
General purposes, hot or cold rolled sheet/plate and strip
EN 10088-1 X6CrNiCuS18-9-2
Not documented
Can EN 10088-2 X6CrMnNiCuN18-12-4-2 Be Substituted With EN 10088-1 X6CrNiCuS18-9-2?
EN 10088-2 X6CrMnNiCuN18-12-4-2 and EN 10088-1 X6CrNiCuS18-9-2 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
EN 10088-2 X6CrMnNiCuN18-12-4-2
0 active listings and RFQs →
EN 10088-1 X6CrNiCuS18-9-2
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between EN 10088-2 X6CrMnNiCuN18-12-4-2 and EN 10088-1 X6CrNiCuS18-9-2?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can EN 10088-2 X6CrMnNiCuN18-12-4-2 be substituted with EN 10088-1 X6CrNiCuS18-9-2?
EN 10088-2 X6CrMnNiCuN18-12-4-2 and EN 10088-1 X6CrNiCuS18-9-2 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.