EN 10088-2 X8CrMnNi19-6-3 vs EN 10088-1 1.4301

Minimal Match — 35% match based on chemical composition and mechanical property overlap.

EN 10088-2 X8CrMnNi19-6-3 (EN 10088-2:2014) and EN 10088-1 1.4301 (EN 10088-1:2014) are both steel grades. Both fall under the Stainless Steel category. EN 10088-2 X8CrMnNi19-6-3 is typically used for general purposes, hot or cold rolled sheet/plate and strip, while EN 10088-1 1.4301 is commonly used for food equipment, chemical vessels, architectural, kitchenware. EN 10088-2 X8CrMnNi19-6-3 is defined under European Standard (EN), originating from Europe, while EN 10088-1 1.4301 is defined under European Standard (EN), originating from Europe.

As per chemical composition, EN 10088-2 X8CrMnNi19-6-3 vs EN 10088-1 1.4301 is a 66.2% match. As per mechanical properties, the match is 0%. Combined, this makes them a minimal match overall at 35%.

Frequently Compared With EN 10088-2 X8CrMnNi19-6-3:
ASTM A959 .- GOST 5632 08X18H10 ASTM A959 201 ASTM A959 202 GOST 5632 06Kh23N28 EN 10088-1 1.4845 IS 1570 (Part 7) 12Cr12MoH GB/T 3280 06Cr19Ni10 EN 10088-1 1.4006 EN 10088-1 1.4401 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoVH
Match Breakdown
CHEMISTRY MATCH
66.2%
MECHANICAL MATCH
0%
OVERALL
35%
Specifications
Property EN 10088-2 X8CrMnNi19-6-3 EN 10088-1 1.4301
Standard EN 10088-2:2014 EN 10088-1:2014
Category Stainless Steel Stainless Steel
C (%) <=0.10 ≤0.07
Si (%) <=1.00 ≤1.00
Mn (%) 5.0-8.0 ≤2.00
P (%) <=0.045 ≤0.045
S (%) <=0.015 ≤0.030
Cr (%) 17.0-20.5 17.5–19.5
Ni (%) 2.00-4.5 8.0–10.5
N (%) <=0.30 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property EN 10088-2 X8CrMnNi19-6-3 EN 10088-1 1.4301
Tensile Strength 600-900 MPa ≥520 MPa
Yield Strength >=400 MPa ≥210 MPa
Elongation >=40% ≥45%
Condition Solution annealed (+AT), cold rolled strip, up to 4 mm thick; Yield Strength is Rp0.2 (transverse), Elongation is A80 for under 3 mm thick Not specified
Hardness Not specified ≤215 HB
Typical Applications
EN 10088-2 X8CrMnNi19-6-3
General purposes, hot or cold rolled sheet/plate and strip
EN 10088-1 1.4301
Food equipment, chemical vessels, architectural, kitchenware
Key Differences
Can EN 10088-2 X8CrMnNi19-6-3 Be Substituted With EN 10088-1 1.4301?
EN 10088-2 X8CrMnNi19-6-3 and EN 10088-1 1.4301 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
EN 10088-2 X8CrMnNi19-6-3
No active listings currently.
EN 10088-1 1.4301
Sheet → (3 listings)
Thickness: 6–6 mm (0.24–0.24 in)
Width: 1250–1250 mm (49.21–49.21 in)
Length: 2500–3300 mm (98.43–129.92 in)
On M-EX Right Now
EN 10088-2 X8CrMnNi19-6-3
0 active listings and RFQs →
EN 10088-1 1.4301
3 active listings and RFQs →
Frequently Asked Questions
What is the difference between EN 10088-2 X8CrMnNi19-6-3 and EN 10088-1 1.4301?
EN 10088-2 X8CrMnNi19-6-3 specifies N which is not specified for EN 10088-1 1.4301.
Can EN 10088-2 X8CrMnNi19-6-3 be substituted with EN 10088-1 1.4301?
EN 10088-2 X8CrMnNi19-6-3 and EN 10088-1 1.4301 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.