EN 10088-2 X8CrMnNi19-6-3 vs ASTM A959 .-

Minimal Match — 35% match based on chemical composition and mechanical property overlap.

EN 10088-2 X8CrMnNi19-6-3 (EN 10088-2:2014) and ASTM A959 .- (ASTM A959:2011) are both steel grades. Both fall under the Stainless Steel category. EN 10088-2 X8CrMnNi19-6-3 is typically used for general purposes, hot or cold rolled sheet/plate and strip, while ASTM A959 .- is commonly used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1). EN 10088-2 X8CrMnNi19-6-3 is defined under European Standard (EN), originating from Europe, while ASTM A959 .- is defined under ASTM International, originating from United States.

As per chemical composition, EN 10088-2 X8CrMnNi19-6-3 vs ASTM A959 .- is a 64.5% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a minimal match overall at 35%.

Frequently Compared With EN 10088-2 X8CrMnNi19-6-3:
GOST 5632 08X18H10 ASTM A959 201 ASTM A959 202 GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4401 EN 10088-1 1.4845 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH
Match Breakdown
CHEMISTRY MATCH
64.5%
MECHANICAL MATCH
No shared data
OVERALL
35%
Specifications
Property EN 10088-2 X8CrMnNi19-6-3 ASTM A959 .-
Standard EN 10088-2:2014 ASTM A959:2011
Category Stainless Steel Stainless Steel
C (%) <=0.10 <=0.030
Si (%) <=1.00 <=1.00
Mn (%) 5.0-8.0 <=1.00
P (%) <=0.045 <=0.040
S (%) <=0.015 <=0.030
Cr (%) 17.0-20.5 18.0-20.0
Ni (%) 2.00-4.5 <=0.50
N (%) <=0.30 <=0.030
Cb (%) Not specified 0.10-0.60
Ti (%) Not specified 0.07-0.30
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property EN 10088-2 X8CrMnNi19-6-3 ASTM A959 .-
Tensile Strength 600-900 MPa Not specified
Yield Strength >=400 MPa Not specified
Elongation >=40% Not specified
Condition Solution annealed (+AT), cold rolled strip, up to 4 mm thick; Yield Strength is Rp0.2 (transverse), Elongation is A80 for under 3 mm thick Not specified
Typical Applications
EN 10088-2 X8CrMnNi19-6-3
General purposes, hot or cold rolled sheet/plate and strip
ASTM A959 .-
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
Key Differences
Can EN 10088-2 X8CrMnNi19-6-3 Be Substituted With ASTM A959 .-?
EN 10088-2 X8CrMnNi19-6-3 and ASTM A959 .- share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
EN 10088-2 X8CrMnNi19-6-3
0 active listings and RFQs →
ASTM A959 .-
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between EN 10088-2 X8CrMnNi19-6-3 and ASTM A959 .-?
ASTM A959 .- specifies Cb, Ti which are not specified for EN 10088-2 X8CrMnNi19-6-3.
Can EN 10088-2 X8CrMnNi19-6-3 be substituted with ASTM A959 .-?
EN 10088-2 X8CrMnNi19-6-3 and ASTM A959 .- share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.