EN 10088-3:2014 X11CrNiMnN19-8-6 Steel: Specifications & Listings
EN 10088-3:2014 X11CrNiMnN19-8-6: X11CrNiMnN19-8-6: austenitic corrosion resisting stainless steel, material number 1.4369. Specified in EN 10088-3:2014.
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Chemical Composition (%)
C
Si
Mn
P
S
Cr
Ni
N
0.07-0.15
0.50-1.00
5.0-7.5
<=0.030
<=0.015
17.5-19.5
6.5-8.5
0.20-0.30
Mechanical Properties
Tensile Strength
750-950 MPa
Yield Strength
>=340 MPa
Elongation
>=35%
Hardness
<=300 HB
Condition
Solution annealed (+AT), conditions 1C, 1E, 1D, 1X, 1G and 2D, thickness or diameter up to 15 mm; Yield Strength is Rp0.2, Elongation is A (longitudinal), hardness for guidance only
More data from EN 10088-3:2014
From the standard
Mechanical properties by thickness or diameter1 size range
Thickness or diameter (mm)
Hardness HBW, max (guidance)
Rp0.2 min (MPa)
Rp1.0 min (MPa)
Rm (MPa)
A min, longitudinal (%)
A min, transverse (%)
KV2 min, longitudinal (J)
KV2 min, transverse (J)
up to 15
300
340
370
750 to 950
35
35
100
60
Solution annealed, conditions 1C, 1E, 1D, 1X, 1G and 2D; for rods only the tensile strength values apply.
Source: EN 10088-3:2014, Table 8
Proof strength at elevated temperature10 temperatures
Temperature (deg C)
Rp0.2 min (MPa)
Rp1.0 min (MPa)
100
225
255
150
200
230
200
185
210
250
175
200
300
165
190
350
155
180
400
-
-
450
-
-
500
-
-
550
-
-
Minimum values, solution annealed (+AT).
Source: EN 10088-3:2014, Table 20
Hot forming and solution annealingguideline temperatures
Hot forming temperature
1150 to 850 deg C
Cooling after hot forming
air
Heat treatment symbol
+AT
Solution annealing temperature
1000 to 1100 deg C
Cooling after solution annealing
water, air
Informative guideline; cooling must be rapid enough to avoid intergranular corrosion.
Source: EN 10088-3:2014, Table A.1