EN 10088-3 X11CrNiMnN19-8-6 vs EN 10088-1 X12CrMnNiN18-9-5

Close Alternative — 70.7% match based on chemical composition and mechanical property overlap.

EN 10088-3 X11CrNiMnN19-8-6 (EN 10088-3:2014) and EN 10088-1 X12CrMnNiN18-9-5 (EN 10088-1:2023) are both steel grades. Both fall under the Stainless Steel category. EN 10088-3 X11CrNiMnN19-8-6 is defined under European Standard (EN), originating from Europe, while EN 10088-1 X12CrMnNiN18-9-5 is defined under European Standard (EN), originating from Europe.

As per chemical composition, EN 10088-3 X11CrNiMnN19-8-6 vs EN 10088-1 X12CrMnNiN18-9-5 is a 70.7% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a close alternative overall at 70.7%.

Frequently Compared With EN 10088-3 X11CrNiMnN19-8-6:
GOST 5632 08X18H10 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4401 EN 10088-1 1.4845 IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12Ni2Mo IS 1570 (Part 7) 12Cr13H ASTM A959 .- GB/T 3280 06Cr19Ni10 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoVH
Match Breakdown
CHEMISTRY MATCH
70.7%
MECHANICAL MATCH
No shared data
OVERALL
70.7%
Specifications
Property EN 10088-3 X11CrNiMnN19-8-6 EN 10088-1 X12CrMnNiN18-9-5
Standard EN 10088-3:2014 EN 10088-1:2023
Category Stainless Steel Stainless Steel
C (%) 0.07-0.15 <=0.15
Si (%) 0.50-1.00 <=1.00
Mn (%) 5.0-7.5 7.5-10.5
P (%) <=0.030 <=0.045
S (%) <=0.015 <=0.015
Cr (%) 17.5-19.5 17.0-19.0
Ni (%) 6.5-8.5 4.0-6.0
N (%) 0.20-0.30 0.05-0.25
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property EN 10088-3 X11CrNiMnN19-8-6 EN 10088-1 X12CrMnNiN18-9-5
Tensile Strength 750-950 MPa Not specified
Yield Strength >=340 MPa Not specified
Elongation >=35% Not specified
Hardness <=300 HB Not specified
Condition Solution annealed (+AT), conditions 1C, 1E, 1D, 1X, 1G and 2D, thickness or diameter up to 15 mm; Yield Strength is Rp0.2, Elongation is A (longitudinal), hardness for guidance only Not specified
Typical Applications
EN 10088-3 X11CrNiMnN19-8-6
General purposes, semi-finished products, bars, rods, wire, sections and bright products
EN 10088-1 X12CrMnNiN18-9-5
Not documented
Can EN 10088-3 X11CrNiMnN19-8-6 Be Substituted With EN 10088-1 X12CrMnNiN18-9-5?
EN 10088-3 X11CrNiMnN19-8-6 and EN 10088-1 X12CrMnNiN18-9-5 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
On M-EX Right Now
EN 10088-3 X11CrNiMnN19-8-6
0 active listings and RFQs →
EN 10088-1 X12CrMnNiN18-9-5
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between EN 10088-3 X11CrNiMnN19-8-6 and EN 10088-1 X12CrMnNiN18-9-5?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can EN 10088-3 X11CrNiMnN19-8-6 be substituted with EN 10088-1 X12CrMnNiN18-9-5?
EN 10088-3 X11CrNiMnN19-8-6 and EN 10088-1 X12CrMnNiN18-9-5 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.