EN 10088-3 X11CrNiMnN19-8-6 vs GOST 5632 08X18H10

Minimal Match — 35% match based on chemical composition and mechanical property overlap.

EN 10088-3 X11CrNiMnN19-8-6 (EN 10088-3:2014) and GOST 5632 08X18H10 (GOST 5632-2014) are both steel grades. Both fall under the Stainless Steel category. EN 10088-3 X11CrNiMnN19-8-6 is typically used for general purposes, semi-finished products, bars, rods, wire, sections and bright products, while GOST 5632 08X18H10 is commonly used for chemical equipment, food processing, general corrosion resistant applications. EN 10088-3 X11CrNiMnN19-8-6 is defined under European Standard (EN) (Europe).

As per chemical composition, EN 10088-3 X11CrNiMnN19-8-6 vs GOST 5632 08X18H10 is a 60.3% match. As per mechanical properties, the match is 0%. Combined, this makes them a minimal match overall at 35%.

Frequently Compared With EN 10088-3 X11CrNiMnN19-8-6:
IS 1570 (Part 7) 12Cr12Ni2Mo IS 1570 (Part 7) 12Cr13H ASTM A959 .- GB/T 3280 06Cr19Ni10 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4401 EN 10088-1 1.4845 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH
Other Stainless Steel Grades to Compare With EN 10088-3 X11CrNiMnN19-8-6:
GOST 5632 06Kh23N28
Match Breakdown
CHEMISTRY MATCH
60.3%
MECHANICAL MATCH
0%
OVERALL
35%
Specifications
Property EN 10088-3 X11CrNiMnN19-8-6 GOST 5632 08X18H10
Standard EN 10088-3:2014 GOST 5632-2014
Category Stainless Steel Stainless Steel
C (%) 0.07-0.15 ≤0.08
Si (%) 0.50-1.00 ≤0.80
Mn (%) 5.0-7.5 ≤2.00
P (%) <=0.030 ≤0.035
S (%) <=0.015 ≤0.020
Cr (%) 17.5-19.5 17.0–19.0
Ni (%) 6.5-8.5 9.0–11.0
N (%) 0.20-0.30 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property EN 10088-3 X11CrNiMnN19-8-6 GOST 5632 08X18H10
Tensile Strength 750-950 MPa ≥520 MPa
Yield Strength >=340 MPa ≥205 MPa
Elongation >=35% ≥40%
Hardness <=300 HB Not specified
Condition Solution annealed (+AT), conditions 1C, 1E, 1D, 1X, 1G and 2D, thickness or diameter up to 15 mm; Yield Strength is Rp0.2, Elongation is A (longitudinal), hardness for guidance only Not specified
Typical Applications
EN 10088-3 X11CrNiMnN19-8-6
General purposes, semi-finished products, bars, rods, wire, sections and bright products
GOST 5632 08X18H10
Chemical equipment, food processing, general corrosion resistant applications
Key Differences
Can EN 10088-3 X11CrNiMnN19-8-6 Be Substituted With GOST 5632 08X18H10?
EN 10088-3 X11CrNiMnN19-8-6 and GOST 5632 08X18H10 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
EN 10088-3 X11CrNiMnN19-8-6
No active listings currently.
GOST 5632 08X18H10
Sheet → (2 listings)
Thickness: 6–6 mm (0.24–0.24 in)
Width: 1250–1250 mm (49.21–49.21 in)
Length: 2500–2700 mm (98.43–106.3 in)
On M-EX Right Now
EN 10088-3 X11CrNiMnN19-8-6
0 active listings and RFQs →
GOST 5632 08X18H10
2 active listings and RFQs →
Frequently Asked Questions
What is the difference between EN 10088-3 X11CrNiMnN19-8-6 and GOST 5632 08X18H10?
EN 10088-3 X11CrNiMnN19-8-6 specifies N which is not specified for GOST 5632 08X18H10.
Can EN 10088-3 X11CrNiMnN19-8-6 be substituted with GOST 5632 08X18H10?
EN 10088-3 X11CrNiMnN19-8-6 and GOST 5632 08X18H10 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.