EN 10088-3:2014 X2CrNiMoCuN25-6-3 Steel: Specifications & Listings

EN 10088-3:2014 X2CrNiMoCuN25-6-3: X2CrNiMoCuN25-6-3: austenitic-ferritic (duplex) corrosion resisting stainless steel, material number 1.4507. Specified in EN 10088-3:2014.

Category: Stainless Steel
Grade Details
GradeEN 10088-3:2014 X2CrNiMoCuN25-6-3
Standard EN 10088-3:2014
ApplicationsGeneral purposes, semi-finished products, bars, rods, wire, sections and bright products
Equivalent / Similar Grades
Grade Standard Region Live on M-EX
ASTM A959 S32760 ASTM A959:2011 USA No activity yet
IS 6603 X02Cr25Ni6Mo3CuN IS 6603:2024 India No activity yet
EN 10088-1 X2CrNiMoCuN25-6-3 EN 10088-1:2014 Europe (CEN) No activity yet
EN 10088-1 X2CrNiMoCuWN25-7-4 EN 10088-1:2014 Europe (CEN) No activity yet
ASTM A959 S32520 ASTM A959:2011 USA No activity yet
ASTM A959 2507 ASTM A959:2011 USA No activity yet
EN 10088-1 X2CrNiMoN25-7-4 EN 10088-1:2014 Europe (CEN) No activity yet
Grade ComparisonCompare With a Specific Grade →
Grade Standard Match
EN 10088-1 X2CrNiMoCuN25-6-3 EN 10088-1:2014 Strong Match
EN 10088-1 X2CrNiMoCuN25-6-3 EN 10088-1:2023 Strong Match
EN 10088-1 X2CrNiMoN25-7-4 EN 10088-1:2014 Strong Match
EN 10088-1 X2CrNiMoN25-7-4 EN 10088-1:2023 Strong Match
ASTM A959 S32520 ASTM A959:2011 Strong Match
EN 10088-1 X2CrNiMoCuWN25-7-4 EN 10088-1:2014 Strong Match
EN 10088-1 X2CrNiMoCuWN25-7-4 EN 10088-1:2023 Strong Match
ASTM A959 2507 ASTM A959:2011 Strong Match
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Chemical Composition (%)
C Si Mn P S Cr Mo Ni N Cu
<=0.030 <=0.70 <=2.00 <=0.035 <=0.015 24.0-26.0 3.0-4.0 6.0-8.0 0.20-0.30 1.00-2.50
Mechanical Properties
Tensile Strength 700-900 MPa
Yield Strength >=500 MPa
Elongation >=25%
Hardness <=270 HB
Condition Solution annealed (+AT), conditions 1C, 1E, 1D, 1X, 1G and 2D, thickness or diameter up to 160 mm; Yield Strength is Rp0.2, Elongation is A (longitudinal), hardness for guidance only

More data from EN 10088-3:2014

From the standard
Mechanical properties by thickness or diameter 1 size range
Thickness or diameter (mm)Hardness HBW, max (guidance)Rp0.2 min (MPa)Rm (MPa)A min, longitudinal (%)KV2 min, longitudinal (J)
up to 160270500700 to 90025100
Solution annealed, conditions 1C, 1E, 1D, 1X, 1G and 2D; for rods only the tensile strength values apply.
Source: EN 10088-3:2014, Table 9
Bright bars, solution annealed 5 size ranges
Thickness or diameter (mm)Rp0.2 min (MPa)Rm (MPa)A5 min, longitudinal (%)KV2 min, longitudinal (J)
up to 10----
over 10 to 16----
over 16 to 40500700 to 105025100
over 40 to 63500700 to 90025100
over 63 to 160500700 to 90025100
Bright bars, conditions 2H, 2B, 2G or 2P; A5 valid for 5 mm and above.
Source: EN 10088-3:2014, Table 14
Proof strength at elevated temperature 4 temperatures
Temperature (deg C)Rp0.2 min, +AT (MPa)
100450
150420
200400
250380
Minimum values.
Source: EN 10088-3:2014, Table 21
Hot forming and solution annealing guideline temperatures
Hot forming temperature
1200 to 1000 deg C
Cooling after hot forming
air
Heat treatment symbol
+AT
Solution annealing temperature
1040 to 1120 deg C
Cooling after solution annealing
water
Informative guideline; cooling must be rapid enough to avoid precipitation.
Source: EN 10088-3:2014, Table A.2

Active EN 10088-3:2014 X2CrNiMoCuN25-6-3 Listings on M-EX (For Sale)

+ Create a Listing for this grade

No active EN 10088-3:2014 X2CrNiMoCuN25-6-3 listings at this time.

Register for Alerts

Buyer RFQs for EN 10088-3:2014 X2CrNiMoCuN25-6-3

+ Post an RFQ for this grade

No open buyer requirements for EN 10088-3:2014 X2CrNiMoCuN25-6-3 at this time.

Register for Alerts