EN 10088-3:2014 X2CrNiMoV13-5-2 Steel: Specifications & Listings
EN 10088-3:2014 X2CrNiMoV13-5-2: X2CrNiMoV13-5-2: martensitic corrosion resisting stainless steel, material number 1.4415. Specified in EN 10088-3:2014.
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Chemical Composition (%)
C
Si
Mn
P
S
Cr
Mo
Ni
Ti
V
<=0.030
<=0.50
<=0.50
<=0.040
<=0.015
11.5-13.5
1.50-2.50
4.5-6.5
<=0.010
0.10-0.50
Mechanical Properties
Tensile Strength
750-900 MPa
Yield Strength
>=650 MPa
Elongation
>=18%
Condition
Annealed (+A), conditions 1C, 1E, 1D, 1X, 1G and 2D, thickness or diameter up to 160 mm; hardness for guidance only
More data from EN 10088-3:2014
From the standard
Mechanical properties by heat treatment condition2 rows
Thickness or diameter (mm)
Condition
Hardness HBW, max (guidance)
Rp0.2 min (MPa)
Rm (MPa)
A min, longitudinal (%)
A min, transverse (%)
KV2 min, longitudinal (J)
KV2 min, transverse (J)
up to 160
+QT750
-
650
750 to 900
18
-
100
-
up to 160
+QT850
-
750
850 to 1000
15
-
80
-
+A = annealed, +QT = quenched and tempered; for rods only the tensile strength values apply.
Source: EN 10088-3:2014, Table 11
Proof strength at elevated temperature7 temperatures
Temperature (deg C)
Rp0.2 min, +QT750 (MPa)
Rp0.2 min, +QT850 (MPa)
100
620
710
150
605
695
200
595
680
250
585
670
300
580
660
350
570
645
400
560
635
Minimum values.
Source: EN 10088-3:2014, Table 23
Hot forming and heat treatment2 conditions
Condition
Annealing temperature (deg C)
Cooling after annealing
Quenching temperature (deg C)
Quenching medium
Tempering temperature (deg C)
+QT750
-
-
950 to 1050
oil, air
600 to 650 + 500 to 550
+QT850
-
-
950 to 1050
oil, air
600 to 650 + 500 to 550
Hot forming 1150 to 900 deg C, cooling: air. Informative guideline.
Source: EN 10088-3:2014, Table A.4