EN 10088-3 X2CrNiMoV13-5-2 vs ASTM A959 444

Related Material — 61.3% match based on chemical composition and mechanical property overlap.

EN 10088-3 X2CrNiMoV13-5-2 (EN 10088-3:2014) and ASTM A959 444 (ASTM A959:2011) are both steel grades. Both fall under the Stainless Steel category. EN 10088-3 X2CrNiMoV13-5-2 is typically used for general purposes, semi-finished products, bars, rods, wire, sections and bright products, while ASTM A959 444 is commonly used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1). EN 10088-3 X2CrNiMoV13-5-2 is defined under European Standard (EN), originating from Europe, while ASTM A959 444 is defined under ASTM International, originating from United States.

As per chemical composition, EN 10088-3 X2CrNiMoV13-5-2 vs ASTM A959 444 is a 61.3% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a related material overall at 61.3%.

Frequently Compared With EN 10088-3 X2CrNiMoV13-5-2:
ASTM A959 .- GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 GOST 5632 08X18H10 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4401 EN 10088-1 1.4845 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr12Ni2Mo
Match Breakdown
CHEMISTRY MATCH
61.3%
MECHANICAL MATCH
No shared data
OVERALL
61.3%
Specifications
Property EN 10088-3 X2CrNiMoV13-5-2 ASTM A959 444
Standard EN 10088-3:2014 ASTM A959:2011
Category Stainless Steel Stainless Steel
C (%) <=0.030 <=0.025
Si (%) <=0.50 <=1.00
Mn (%) <=0.50 <=1.00
P (%) <=0.040 <=0.040
S (%) <=0.015 <=0.030
Cr (%) 11.5-13.5 17.5-19.5
Mo (%) 1.50-2.50 1.75-2.50
Ni (%) 4.5-6.5 <=1.00
Ti (%) <=0.010 Not specified
V (%) 0.10-0.50 Not specified
N (%) Not specified <=0.035
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property EN 10088-3 X2CrNiMoV13-5-2 ASTM A959 444
Tensile Strength 750-900 MPa Not specified
Yield Strength >=650 MPa Not specified
Elongation >=18% Not specified
Condition Annealed (+A), conditions 1C, 1E, 1D, 1X, 1G and 2D, thickness or diameter up to 160 mm; hardness for guidance only Not specified
Typical Applications
EN 10088-3 X2CrNiMoV13-5-2
General purposes, semi-finished products, bars, rods, wire, sections and bright products
ASTM A959 444
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
Key Differences
Can EN 10088-3 X2CrNiMoV13-5-2 Be Substituted With ASTM A959 444?
EN 10088-3 X2CrNiMoV13-5-2 and ASTM A959 444 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
EN 10088-3 X2CrNiMoV13-5-2
0 active listings and RFQs →
ASTM A959 444
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between EN 10088-3 X2CrNiMoV13-5-2 and ASTM A959 444?
EN 10088-3 X2CrNiMoV13-5-2 specifies Ti, V which are not specified for ASTM A959 444. ASTM A959 444 specifies N which is not specified for EN 10088-3 X2CrNiMoV13-5-2.
Can EN 10088-3 X2CrNiMoV13-5-2 be substituted with ASTM A959 444?
EN 10088-3 X2CrNiMoV13-5-2 and ASTM A959 444 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.